PA66 Resin Containing 30% Glass Bead15% PTFE Low Extractable Healthcare Wear Resis

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA66-RBL36XXJ
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

PA66resin containing 30% glass bead15% PTFE Low Extractable Healthcare Wear Resis
 Heat-conducting nylon

Product Description

Product Description
LNP LUBRICOMP RBL36XXJ compound is based on Nylon 6/6 resin containing 30% glass bead, 15% PTFE. Added features of this grade include: Low Extractable, Healthcare, Wear Resistant, Food Contact compliant.
General
Form	Resin Pellets
Filler                                         30 % Glass Bead                15 % PTFE
Feature	Low Warpage   Abrasion Resistant		Fda   Low Extractables		Good Dimensional   Internally Lubricated
Uses	Consumer                         Healthcare   Building and Construction				Packaging
Physical                                                                                 Nominal Value                                       Test Method
Density / Specific Gravity 1.49                                                        ASTM D792 1.49 g/cm³                                            ISO 1183
Moisture Absorption
23 °C;50% RH/24 hrs                                                          0.41 %                                                     ASTM D570
50% RH;23 °C                                                                      0.58 %                                                     ISO 62
Mold Shrinkage, Flow(24 hrs)                                              2 - 4 %                                                    ASTM D955
Mold Shrinkage, XFlow(24 hrs)                                            1 - 3 %                                                    ASTM D955
Wear Factor Washer                                                           41 10^-10 in^5-min/ft-lb-hr						ASTM D3702 Modified: Manual
Wear Factor, Ring                                                                8 10^-10 in^5-min/ft-lb-hr						ASTM D3702 Modified: Manual
Dynamic Cof                                                                         0.47					ASTM D3702 Modified: Manual
Static Cof                                                                              0.44					ASTM D3702 Modified: Manual
Mechanical		Nominal Value			Test Method
Izod Impact, Unnotched
23 °C		435 J/m			ASTM D4812
80*10*4;23 °C		27 kJ/m²			ISO 180/1U
Izod Impact, Notched
23 °C		51 J/m			ASTM D256
80*10*4;23 °C		5 kJ/m²			ISO 180/1A
Multiaxial Impact		1 J			ISO 6603
Instrumented Dart Impact, Total Energy(23 °C)		5 J			ASTM D3763
Tensile Stress, Break
5 mm/min;Type I		64 MPa			ASTM D638
5 mm/min		64 MPa			ISO 527
Tensile Strain, Yield(5 mm/min;Type I)		8.5 %			ASTM D638
Tensile Strain, Break
5 mm/min;Type I		10 %			ASTM D638
5 mm/min		8.3 %			ISO 527
Tensile Modulus
5 mm/min		3990 MPa			ASTM D638
1 mm/min		3930 MPa			ISO 527
Flexural Modulus
1.3 mm/min;50 mm;span		3740 MPa			ASTM D790
2 mm/min		3560 MPa			ISO 178
Flexural Stress		107 MPa			ISO 178
Thermal		Nominal Value			Test Method
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa		236 °C 83 °C			ASTM D648
CTE, Flow(-30 - 30 °C)		6.9e-05 1/°C			ASTM D696
CTE, XFlow(-30 - 30 °C)		8.3E-05 1/°C			ASTM D696
HDT/Bf(0.45)		203 °C			ISO 75/Bf
HDT/Af(1.8)		73 °C			ISO 75/Af
Processing				Nominal Value
Drying Temperature<Injection>				80 °C
Drying Time<Injection>				4 hrs
Maximum Moisture Content<Injection>				0.15 - 0.25 %
Melt Temperature<Injection>				280 - 305 °C
Front, Zone 3 Temperature<Injection>				295 - 305 °C
Middle, Zone 2 Temperature<Injection>				280 - 295 °C
Rear, Zone 1 Temperature<Injection>				265 - 275 °C
Mold Temperature<Injection>				95 - 110 °C
Back Pressure<Injection>				0.2 - 0.3 MPa
Screw Speed <Injection>					30 - 60 rpm

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 