Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
General | ||||
Form | Resin Pellets | |||
Filler | 20% glass fiber | |||
Feature |
Good Hardness Lds |
Non-Brominated & Non- Chlorinated Flame Retardant Structural |
Non-Chlorinated Circuit Solution |
|
Usage | Consumer Laser Direct Structuring Building and Construction |
Electrical | ||
Physical | Nominal Value | Test Method | ||
Melt Flow Rate[MFR] 300 °C;2.16 kgf 300 °C;1.2 kgf |
17 g/10min 10 g/10min |
ASTM D1238 | ||
Density / Specific Gravity | 1.4 g/cm³ | ASTM D792 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched | ||
23 °C | 80 J/m | ASTM D256 |
80*10*4;23 °C | 8 kJ/m² | ISO 180/1A |
Izod Impact, Unnotched | ||
23 °C | 450 J/m | ASTM D4812 |
80*10*4;23 °C | 26 kJ/m² | ISO 180/1U |
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 8 kJ/m² | ISO 179 1eA |
C harpy Impact, Unnotched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 30 kJ/m² | ISO 179 1eU |
Tensile Stress, Break | ||
5 mm/min;Type I | 85 MPa | ASTM D638 |
5 mm/min | 86 MPa | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 2.5 % | ASTM D638 |
5 mm/min | 2.5 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 7000 MPa | ASTM D638 |
1 mm/min | 6900 MPa | ISO 527 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 6000 MPa | ASTM D790 |
2 mm/min | 6400 MPa | ISO 178 |
Flexural Strength | ||
1.3 mm/min;50 mm;span | 125 MPa | ASTM D790 |
2 mm/min | 130 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
124 °C 118 °C |
ASTM D648 |
Electrical | Nominal Value | Test Method |
Processing | Nominal Value | |
Drying Temperature<Injection> | 110 - 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Melt Temperature<Injection> | 290 - 310 °C | |
Nozzle Temperature<Injection> | 285 - 310 °C | |
Front, Zone 3 Temperature<Injection> | 285 - 310 °C | |
Middle, Zone 2 Temperature<Injection> | 285 - 310 °C | |
Rear, Zone 1 Temperature<Injection> | 285 - 310 °C | |
Mold Temperature<Injection> | 100 - 130 °C | |
Back Pressure<Injection> | 0.1 - 0.3 MPa | |
Screw Speed <Injection> | 50 - 150 rpm |