Polyamide 6 (PA6) Based Compound Heat Stabilised. Mineral Filler UL 94 Classified

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA6-FR H2 CE/25-V2HF
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Polyamide 6 (PA6) based compound Heat stabilised Mineral filler UL 94 V-2 classified
 Heat-conducting nylon

Product Description

Polyamide 6 (PA6) based compound. Heat stabilised. Mineral filler. UL 94 V-2 classified, free of halogens-based flame retardants and red phosphorous.
General
Form	Resin Pellets
Filler	25 % Mineral
Feature		Chlorinated Flame   Retardant
Physical		Nominal Value                                      Test Method
Density / Specific Gravity		1.33 g/cm³
Molding Shrinkage, Across	Flow(2 mm;60 MPa)	0.65 - 0.85 %
Molding Shrinkage, Flow(2	mm;60 MPa)	0.55 - 0.75 %
Water Absorption(23 °C;24 hr)		0.32 %
Mechanical		Nominal Value	Test Method
Tensile Modulus 23 °C 60 °C 90 °C 120 °C 150 °C		5200 MPa 2200 MPa 1300 MPa 750 MPa 500 MPa	ISO 527-1/2
Tensile Stress, Break 23 °C 60 °C 90 °C 120 °C 150 °C		65.0 MPa 45.0 MPa 30.0 MPa 20.0 MPa 15.0 MPa	ISO 527-2/5
Elongation at Break 23 °C 60 °C 90 °C 120 °C 150 °C		2.5 % 3.5 % 6.5 % 12 % 20 %	ISO 527-2/5
C harpy Notched Impact Strength(23 °C)		3.0 kJ/m²	ISO 179 1eA
C harpy Unnotched Impact Strength(23 °C)		30 kJ/m²	ISO 179 1eU
Thermal		Nominal Value	Test Method
Heat Deflection Temperature Unannealed;0.45 MPa Unannealed;1.8 MPa		200 °C 120 °C
Continuous Use Temperature(2.0e+4 hr)		80.0 °C
Vicat Softening Temperature		205 °C	ISO 306/B50
CTE, Flow(30 - 100 °C)		3.5E-5 cm/cm/°C
Flame Rating 0.75 mm 1.5 mm 3 mm		V-2 V-2 V-2
Glow Wire Flammability Index(1 mm)		960 °C
Oxygen Index		27 %	ASTM D2863
Electrical		Nominal Value                                      Test Method
Comparative Tracking Index(Solution A, Without surfactant)		550 V

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 