Glass fibre reinforced injection moulding grade for machinery components
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | ||||||
Glass fibre reinforced injection moulding grade for machinery components and housings of high stiffness and dimensional stability such as coil formers and bearing cages. Also used for electrically insulating parts. | ||||||
General | ||||||
Form | Resin Pellets | |||||
Filler | 25 % Glass Fiber | |||||
Feature | Good Dimensional Ec 1907/2006 (Reach) |
Good Hardness | Fuel Resistant | |||
UL Yellow Card E41871-233729 | ||||||
Uses Electronic Insulation Housing Mechanical Parts | ||||||
Physical | Nominal Value | Test Method | ||||
Density, dry | 1.32 g/cm³ | ISO 1183 | ||||
Dry: Apparent Density, Bulk | 0.70 g/cm³ | No Standard | ||||
Dry: Melt Volume-Flow Rate, MVR(275 °C;5 kg) | 50 cm³/10 min | ISO 1133 | ||||
Dry: Molding Shrinkage, Across Flow | 1.1 % | ISO 294-4 | ||||
Dry: Molding Shrinkage, Flow | 0.60 % | ISO 294-4 | ||||
Dry: Water Absorption, Saturation(23 °C) | 5.7 - 6.3 % | ISO 62 | ||||
Dry: Water Absorption, Equilibrium(50% RH;23 °C) | 1.7 - 2.1 % | ISO 62 | ||||
Dry: Viscosity Number, (96% H2SO4) | 145 cm³/g | ISO 307 | ||||
Dry: Mold Shrinkage, Constrained(TW = 80 °C;107*47*1;5 mm;TM = 290 °C) | 0.55 % | |||||
Mechanical | Nominal Value | Test Method | ||||
Dry: Tensile Modulus | 8600 MPa | ISO 527-2 | ||||
Condition: Tensile Modulus | 6500 MPa | ISO 527-2 | ||||
Dry: Tensile Stress, Break | 175 MPa | ISO 527-2 | ||||
Condition: Tensile Stress, Break | 120 MPa | ISO 527-2 | ||||
Dry: Tensile Strain, Break | 3.0 % | ISO 527-2 | ||||
Condition: Tensile Strain, Break | 6.0 % | ISO 527-2 | ||||
Condition: Tensile creep modulus(1.0e+3 hr;23 °C;strain < = 0.5%) | 4300 MPa | ISO 899-1 | ||||
Dry: Flexural Modulus | 7600 MPa | ISO 178 | ||||
Condition: Flexural Modulus | 6000 MPa | ISO 178 | ||||
Dry: Flexural Stress | 260 MPa | ISO 178 | ||||
Condition: Flexural Stress | 200 MPa | ISO 178 | ||||
Dry: Charpy Notched Impact Strength -30 °C 23 °C |
9.0 kJ/m² 12 kJ/m² |
ISO 179 1eA | ||||
Condition: Charpy Notched Impact Strength -30 °C 23 °C |
7.7 kJ/m² 10 kJ/m² |
ISO 179 1eA | ||||
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
55 kJ/m² 65 kJ/m² |
ISO 179 1eU | ||||
Condition: Charpy Unnotched Impact Strength -30 °C 23 °C |
50 kJ/m² 90 kJ/m² |
ISO 179 1eU | ||||
Dry: Notched Izod Impact Strength -30 °C 23 °C |
8.9 kJ/m² 9.7 kJ/m² |
ISO 180/1A | ||||
Notched Izod Impact Strength: condition -30 °C 23 °C |
8.4 kJ/m² 12 kJ/m² |
ISO 180/1A | ||||
Thermal | Nominal Value | Test Method | ||||
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
260 °C 245 °C |
ISO 75-2/B ISO 75-2/A |
||||
Dry: Melting Temperature | 260 °C | ISO 11357-3 | ||||
Dry: CLTE, Flow(23 - 80 °C) | 3.3E-5 cm/cm/°C | ISO 11359-2 | ||||
Dry: CLTE, Transverse(23 - 80 °C) | 7.5E-5 - 8.5E-5 cm/cm/°C | ISO 11359-2 | ||||
Dry: Specific Heat | 1240 J/kg/°C | No Standard | ||||
Dry: Thermal Conductivity | 0.34 W/m-K | DIN 52612 | ||||
Dry: Maximum Service Temperature - short cycle operation | 240 °C | |||||
Dry: Temperature Index - at 50% loss of tensile strength 5.0e+3 h 2.0e+4 h |
165 °C 135 °C |
IEC 60216 | ||||
Dry: Flammability Classification(1.6 mm) | HB | IEC 60695-11-10/- 20 | ||||
Dry: Halogen Content | < 100 mg/kg | Internal Method | ||||
Electrical | Nominal Value | Test Method | ||||
Condition: Surface resistivity | 1.0E+10 ohms | IEC 60093 | ||||
Dry: Volume Resistivity | 1.0e+15 ohms ·cm | IEC 60093 | ||||
Condition: Volume resistivity | 1.0E+12 ohms ·cm | IEC 60093 | ||||
Dry: Relative permittivity(1.0e+6 Hz) | 3.70 | IEC 60250 | ||||
Condition: Relative Permittivity(1.0e+6 Hz) | 4.30 | IEC 60250 | ||||
Dry: Dissipation Factor(1.0e+6 Hz) | 0.021 | IEC 60250 | ||||
Condition: Dissipation factor(1.0e+6 Hz) | 0.081 | IEC 60250 | ||||
Dry: Comparative Tracking Index, Solution A | 550 V | IEC 60112 | ||||
Processing | Nominal Value | |||||
Drying Temperature<Injection> | 80 °C | |||||
Drying Time<Injection> | 4.0 hr | |||||
Suggested Max Moisture<Injection> | 0.15 % | |||||
Hopper Temperature<Injection> | 80 °C | |||||
Rear Temperature<Injection> | 290 °C | |||||
Middle Temperature<injection> | 290 °C | |||||
Front Temperature<Injection> | 290 °C | |||||
Nozzle Temperature<Injection> | 290 °C | |||||
Processing Temp, Melt<Injection> | 280 - 300 °C | |||||
Mold Temperature<Injection> | 80 - 90 °C | |||||
Residence Time<Injection> | < 10.0 min | |||||
Screw Speed <Injection> | < 18 m/min |