Polyamine Nylon 66 33% Glass Reinforced Heat Stabilized Automotive

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA66-70G33HS1L NC010
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Polyamine Nylon 66 33% Glass Reinforced Heat Stabilized  Automotive
 Heat-conducting nylon

Product Description

Product Description
33% Glass Reinforced, Heat Stabilized, Polyamide 66. Automotive Specifications : ASTM D6779 PA012G35, CHRYSLER MS-DB-41 CPN2043, CHRYSLER MS-DB-41 CPN2224 Color: Color As Noted On Drawing, DELPHI 7826921, DELPHI DM 7409, DELPHI DX300293, DELPHI M-4692, DELPHI M-53103, FORD ESE-M4D287-A, FORD ESE-M4D287-B, FORD WSK-M4D663-A, FORD WSK-M4D673-A, FORD WSS-M4D673-B1, GM GMP.PA66.013, GM GMW3038P-PA66-GF35H.
General
Form		Resin Pellets
Filler		33 % Glass Fiber
Feature		Good Thermal
UL Yellow Card	E41938-234409
Physical					Nominal Value		Test Method
Density, dry					1.39 g/cm³		ISO 1183
Dry: Molding Shrinkage, Across Flow					1.1 %		ISO 294-4
Dry: Molding Shrinkage, Flow					0.30 %		ISO 294-4
Dry: Water Absorption(24 hr;23 °C)					1.2 %		ISO 62
Dry: Water Absorption, Saturation(23 °C;2 mm)					5.7 %		ISO 62
Dry: Water Absorption, Equilibrium(50% RH;23 °C;2 mm)					1.8 %		ISO 62
Dry: Fogging, G-value, condensate					3.0E-4 g		ISO 6452
Dry: Emission of Organic Compounds					6.00 µgC/g		VDA 277
Dry: Odor					4.50		VDA 270
Mechanical					Nominal Value		Test Method
Dry: Tensile Modulus					11000 MPa		ISO 527-2
Condition: Tensile Modulus					8000 MPa		ISO 527-2
Dry: Tensile Stress, Break					200 MPa		ISO 527-2
Condition: Tensile Stress, Break					140 MPa		ISO 527-2
Dry: Tensile Strain, Break					3.5 %		ISO 527-2
Condition: Tensile Strain, Break					5.0 %		ISO 527-2
Condition: Tensile creep modulus 1 hr 1.0e+3 hr					8000 MPa 5500 MPa		ISO 899-1
Dry: Flexural Modulus					9500 MPa		ISO 178
Condition: Flexural Modulus					6000 MPa		ISO 178
Dry: Flexural Stress					290 MPa		ISO 178
Condition: Flexural Stress			200 MPa			ISO 178
Dry: Charpy Notched Impact Strength -40 °C -30 °C 23 °C			10 kJ/m² 10 kJ/m² 13 kJ/m²			ISO 179 1eA
Condition: Charpy Notched Impact Strength -40 °C -30 °C 23 °C			10 kJ/m² 10 kJ/m² 17 kJ/m²			ISO 179 1eA
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C			70 kJ/m² 85 kJ/m²			ISO 179 1eU
Condition: Charpy Unnotched Impact Strength -30 °C 23 °C			75 kJ/m² 100 kJ/m²			ISO 179 1eU
Dry: Notched Izod Impact Strength -40 °C -30 °C 23 °C			10 kJ/m² 10 kJ/m² 12 kJ/m²			ISO 180/1A
Notched Izod Impact Strength: condition -40 °C -30 °C 23 °C			10 kJ/m² 10 kJ/m² 15 kJ/m²			ISO 180/1A
Dry: Unnotched Izod Impact Strength -30 °C 23 °C			70 kJ/m² 80 kJ/m²			ISO 180/1U
Condition: Unnotched Izod Impact Strength -30 °C 23 °C			70 kJ/m² 90 kJ/m²			ISO 180/1U
Thermal			Nominal Value			Test Method
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa			261 °C 252 °C			ISO 75-2/B ISO 75-2/A
Dry: Glass Transition Temperature(10 °C;min)			80.0 °C			ISO 11357-2
Dry: Melting Temperature(10 °C;min)			262 °C			ISO 11357-3
Dry: CLTE, Flow -40 - 23 °C 55 - 160 °C			1.8E-5 cm/cm/°C 2.4E-5 cm/cm/°C 1.3E-5 cm/cm/°C			ISO 11359-2
Dry: CLTE, Transverse -40 - 23 °C 55 - 160 °C			8.3E-5 cm/cm/°C 6.5E-5 cm/cm/°C 1.4E-4 cm/cm/°C			ISO 11359-2
Dry: Specific Heat Capacity			1330 J/kg/°C
Dry: Burning rate(1 mm;FMVSS 302)			28 mm/min			ISO 3795
Dry: Flame Rating 0.75 mm 1.5 mm			HB HB			UL 94;IEC 60695- 11-10;-20
Dry: Oxygen index			24 %			ISO 4589-2
Dry: FMVSS Flammability			SE/B			FMVSS 302
Dry: Fogging, F-value, refraction			95 %			ISO 6452
Spec. heat capacity of melt			2210 J/(kg k)
Thermal conductivity of melt			0.22 w/(mk)
Dry: RTI, electrical 0.75 mm 1.5 mm			140 °C 140 °C			UL 7468
RTI, electrical(3 mm)			141 °C			UL 7468
RTI, impact 0.75 mm 3 mm			125 °C 125 °C			UL 7468
Dry: RTI, impact(1.5 mm)			125 °C			UL 7468
RTI, strength 0.75 mm 3 mm			140 °C 140 °C			UL 7468
Dry: RTI, strength(1.5 mm)			140 °C			UL 7468
Dry: Glow Wire Flammability Index 0.75 mm 1.5 mm 3 mm			725 °C 700 °C 800 °C			IEC 60695-2-12
Dry: Glow Wire Ignition Temperature 0.75 mm 1.5 mm 0.75 mm			750 °C 725 °C 825 °C			IEC 60695-2-13
Dry: Thermal Conductivity of Melt			0.22 W/m-K
Dry: Specific Heat Capacity of Melt			2210 J/kg/°C
Electrical			Nominal Value			Test Method
Condition: Surface resistivity			1.0E+15 ohms			IEC 62631-3-2
Dry: Volume Resistivity			1E+11 ohms ·cm			IEC 62631-3-1
Condition: Volume resistivity			1E+7 ohms ·cm			IEC 62631-3-1
Dry: Relative permittivity 1.0e+6 Hz 100 Hz			4.00 4.20			IEC 62631-2-1
Dry: Dissipation Factor 100 Hz 1.0e+6 Hz			0.010 0.015			IEC 62631-2-1
Dry: Comparative Tracking Index[CTI](3 mm)			PLC 1			UL 746
Dry: Comparative Tracking Index			400 V			IEC 60112
Processing				Nominal Value
Drying Temperature<Injection>				80 °C
Drying Time - Desiccant Dryer<Injection>				2.0 - 4.0 hr
Suggested Max Moisture<Injection>				0.20 %
Processing Temp, Melt<Injection>				285 - 305 °C
Melt Temperature, Optimum<Injection>				295 °C
Mold Temperature<Injection>				70 - 120 °C
Mold Temperature, Optimum<Injection>				100 °C
Holding Pressure<Injection>				50.0 - 100 MPa
Drying Recommended <Injection>				YES
Hold Pressure Time<Injection>				3.00 s/mm
Maximum Screw Tangential Speed <Injection>				12 m/min
Dry: Ejection Temperature				210 °C

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 