Plastic Raw Materia Ladvanced Resin Is an Ignition-Resistant PC/ABS Blend

• Feature: Plastics
• CAS No.: 63440-93-7
• Formula: C24h24o8
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC/ABS-7700
• EINECS: 618-371-8
• Material: Polybutylene Terephthalate/PBT
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Natural Color
• Place of Origin: Guangdong, China
• Use: Radiator Front Cover.Automotive Parts
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Delivery Time: in 7 Days
• Applications: Appliance Handles, Spotlights, Electric Motors.
• Glass Fiber: %
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

 Plastic Raw Materia lAdvanced Resin is an ignition-resistant PC/ABS blend 
   

 

Product Description
7700 SK Advanced Resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. This grade has been tested to ISO 10993 Parts 5 & 10 and is suitable for skin contact applications. It has superior processability for injection molding applications. This grade has excellent aesthetics,   is UV stabilized and is available in custom colors.Main Characteristics: Tested under ISO 10993 (Parts 5 & 10) ; UV stabilized; RoHS Compliant; Applications: Medical equipment housings; Consumer Electronics;Wearable devices
General
Form	Resin Pellets
			Non-Brominated & Non-
Feature		Good Surface Appearance  High Impact	Chlorinated Flame   Retardant
Physical		Nominal Value	Test Method
Density / Specific Gravity		1.17 g/cm³ 1.18 g/cm³	ASTM D792 ISO 1183/B
Melt Mass-Flow Rate, MFR
230 °C;3.8 kg		11 g/10min	ASTM D1238
240 °C;5 kg		20 g/10min	ASTM D1238
260 °C;2.16 kg		13 g/10min	ISO 1133
Molding Shrinkage, Flow		0.40 - 0.60 %
Rockwell Hardness, R-Scale,		Injection Molded(3.2 mm)    120	ASTM D785

 

Mechanical	Nominal Value	Test Method
Tensile Modulus, injection molded
3.2 mm	2620 MPa	ASTM D638
4 mm	2560 MPa	ISO 527-2/1
Tensile Strength, Yield, Injection molded
3.2 mm	60.0 MPa	ASTM D638
4 mm	55.0 MPa	ISO 527-2/50
Tensile Strength, Break, Injection molded
3.2 mm	48.3 MPa	ASTM D638
4 mm	45.0 MPa	ISO 527-2/50
Tensile Elongation, Yield, Injection Molded
3.2 mm	3.8 %	ASTM D638
4 mm	3.8 %	ISO 527-2/50
Tensile Elongation, Break, Injection Molded
3.2 mm	65 %	ASTM D638
4 mm	43 %	ISO 527-2/50
Flexural Modulus, Injection Molded(3.2 mm)	2690 MPa	ASTM D790
Flexural Strength, Injection Molded(3.2 mm)	96.5 MPa	ASTM D790
C harpy Notched Impact Strength, Injection Molded -30 °C 23 °C	15 kJ/m² 40 kJ/m²	ISO 179 1eA
Notched Izod Impact, Injection Molded
3.2 mm;-18 °C	200 J/m	ASTM D256
23 °C;3.2 mm	480 J/m	ASTM D256
-30 °C	14 kJ/m²	ISO 180/1A
23 °C	50 kJ/m²	ISO 180/1A
Notched Izod Impact(-7 °C)	440 J/m	ASTM D256

 

Thermal	Nominal Value	Test Method
Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa 0.45 MPa 1.8 MPa	90.6 °C 79.4 °C 88.0 °C 77.0 °C	ASTM D648 ASTM D648 ISO 75-2/B ISO 75-2/A
Vicat Softening Temperature 120 °C/h;10 N;Rate B;Loading 1	104 °C 94.0 °C	ISO 306/B50
CLTE, Flow(-40 - 40 °C)	6.8E-5 cm/cm/°C	ASTM D696
CLTE, Transverse(-40 - 40 °C)	6.8E-5 cm/cm/°C	ASTM D696
Flame Rating 1.5 mm 2 mm 2.5 mm	V-0 5VB 5VA	UL 94
Glow Wire Flammability Index 1.5 mm 2 mm 2.5 mm 3 mm	925 °C 925 °C 925 °C 950 °C	IEC 60695-2-12
Oxygen Index	28 %	ASTM D2863
Electrical	Nominal Value	Test Method
Surface Resistivity	5.2E+15 ohms	IEC 60093
Volume Resistivity	1.0E+18 ohms ·cm	IEC 60093
Electric Strength, in Oil 1.6 mm 3.2 mm	26 kV/mm 18 kV/mm	IEC 60243-1
Relative Permittivity 100 Hz 1.0e+6 Hz	2.86 2.80	IEC 60250
Dissipation Factor 100 Hz 1.0e+6 Hz	4.0E-3 7.0E-3	IEC 60250

 

Processing	Nominal Value
Drying Temperature<Injection>	82 - 88 °C
Drying Time<Injection>	3.0 - 4.0 hr
Processing Temp, Melt<Injection>	238 - 274 °C
Mold Temperature<Injection>	60 - 91 °C

          

Company Profile

Product Parameters

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry