Product Description | |||||
Ultramid A3XZG5 is an impact-modified, 25% glass fiber reinforced injection molding PA66 grade with improved flame retardance. Flame retardant based on red phosphorus.ApplicationsTypical applications include components with high stiffness, dimensional stability and enhanced impact strength such as electrical switches. | |||||
General | |||||
Form | Resin | Pellets | |||
Filler | 25 % | Glass Fiber | |||
UL Yellow Card E41871-233756 | |||||
Automotive PV Junction Box |
Pv Connector | Switches | |||
Physical | Nominal Value | Test Method | |||
Density, dry | 1.32 g/cm³ | ISO 1183 | |||
Dry: Water Absorption, Saturation(23 °C) | 5.0 % | ISO 62 | |||
Dry: Water Absorption, Equilibrium(50% RH;23 °C) | 1.2 % | ISO 62 | |||
Outdoor Suitability | 1 | UL 746C | |||
Mechanical | Nominal Value | Test Method | |||
Dry: Tensile Modulus(23 °C) | 6500 MPa | ISO 527-2 | |||
Condition: Tensile Modulus(23 °C) | 4500 MPa | ISO 527-2 | |||
Dry: Tensile Stress, Break(23 °C) | 105 MPa | ISO 527-2 | |||
Condition: Tensile Stress, Break(23 °C) | 70.0 MPa | ISO 527-2 | |||
Dry: Tensile Strain, Break(23 °C) | 6.0 % | ISO 527-2 | |||
Condition: Tensile Strain, Break(23 °C) | 11 % | ISO 527-2 | |||
Dry: Flexural Modulus(23 °C) | 5500 MPa | ISO 178 | |||
Dry: Charpy Notched Impact Strength(23 °C) | 25 kJ/m² | ISO 179 | |||
Condition: Charpy Notched Impact Strength(23 °C) | 30 kJ/m² | ISO 179 | |||
Dry: Charpy Unnotched Impact Strength(23 °C) | 90 kJ/m² | ISO 179 | |||
Condition: Charpy Unnotched Impact Strength(23 °C) | 100 kJ/m² | ISO 179 |
Thermal | Nominal Value | Test Method |
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
250 °C 240 °C |
ISO 75-2/B ISO 75-2/A |
Dry: Melting Temperature, DSC | 260 °C | ISO 3146 |
Dry: RTI Elec 0.75 mm 1.5 mm 3 mm |
120 °C 120 °C 120 °C |
UL 746 |
Dry: RTI Imp 0.75 mm 1.5 mm 3 mm |
115 °C 115 °C 115 °C |
UL 746 |
Dry: RTI Str 1.5 mm 3 mm |
130 °C 130 °C |
UL 746 |
Dry: Flame Rating 0.75 mm 1.5 mm 3 mm |
HB V-0 V-0 - 5VA |
UL 94 |
Electrical | Nominal Value | Test Method |
Dry: Dielectric Constant(1.0e+6 Hz) | 3.80 | IEC 60250 |
Dry: Dissipation Factor(1.0e+6 Hz) | 0.020 | IEC 60250 |
Condition: Dissipation factor(1.0e+6 Hz) | 0.030 | IEC 60250 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.050 % | |
Processing Temp, Melt<Injection> | 285 - 300 °C | |
Mold Temperature<Injection> | 80 - 90 °C | |
Injection Pressure<Injection> | 3.50 - 12.5 MPa | |
Injection Rate<Injection> | Fast |