| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 32131-17-2 |
| Formula: | (C12h22n2o2)N |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier polyamide 6 based on a non-phosphorous and Non-halogenatedflame retardant system
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||||
| TECHNYL PROTECT C 52G1 MX25 WT 9003 is a polyamide 6 based on a non-phosphorous and Non-halogenated flame retardant system, reinforced with 25% of mineral filler, heat stabilized, for injection moulding. This phosphorus and halogen free flame retardant grade offers a robust glow wire resitance. |
||||
| General | ||||
| Form Resin Pellets | ||||
| Filler 25 % Mineral | ||||
| Non-Brominated & Non- | ||||
| Feature | Chlorinated Flame Retardant |
|||
| Laser Markable | ||||
| Uses Electrical | ||||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.38 g/cm³ | ISO 1183 | ||
| Water Absorption(24 hr;23 °C) | 1.1 % | ISO 62 | ||
| Water Absorption at Saturation(24 hr;23 °C) | 5.6 % | ISO 62 | ||
| Molding shrinkage, parallel(50% RH;23 °C;72 hr) | 0.3 % | ISO 2577;ISO 294- 4 | ||
| Molding shrinkage, normal(50% RH;23 °C;72 hr) | 0.65 % | ISO 2577;ISO 294- 4 | ||
| Mechanical | Nominal Value | Test Method | ||
| Dry: Tensile Modulus(1 mm/min) | 7600 MPa | ISO 527-1/-2 | ||
| Condition: Tensile Modulus(1 mm/min) | 2800 MPa | ISO 527-1/-2 | ||
| Dry: Stress at break | 90 MPa | ISO 527-1/-2 | ||
| Condition: Stress at break | 35 MPa | ISO 527-1/-2 | ||
| Dry: Strain at break | 2.2 % | ISO 527-1/-2 | ||
| Condition: Strain at break | 30 % | ISO 527-1/-2 | ||
| Dry: Flexural Modulus(2 mm/min) | 5500 MPa | ISO 178 | ||
| Condition: Flexural Modulus(2 mm/min) | 2900 MPa | ISO 178 | ||
| Dry: Flexural Strength(2 mm/min) | 100 MPa | ISO 178 | ||
| Condition: Flexural Strength(2 mm/min) | 60 MPa | ISO 178 | ||
| Dry: Charpy Impact Strength(23 °C) | 30 kJ/m² | ISO 179/1eU | ||
| Condition: Charpy Impact Strength(23 °C) | 70 kJ/m² | ISO 179/1eU | ||
| C harpy Impact Strength, Unnotched(- 30 °C) | 30 kJ/m² | ISO 179/1eU | ||
| Dry: Charpy Notched Impact Strength(23 °C) | 3 kJ/m² | ISO 179/1eA | ||
| Condition: Charpy Notched Impact Strength(23 °C) | 3 kJ/m² | ISO 179/1eA | ||
| C harpy Notched Impact Strength(- 30 °C) | 1.5 kJ/m² | ISO 179/1eA | ||
| Thermal | Nominal Value | Test Method | ||
| Melting Temperature(10 °C/min) | 220 °C | ISO 11357-1 | ||
| Temp. of deflection under load 0.45 MPa 1.8 MPa |
200 °C 120 °C |
ISO 75 | ||
| Flammability 0.75 mm 1.5 mm 3 mm |
V-2 V-2 V-2 |
UL 94 | ||
| Glow Wire Flammability Index 1.5 mm 3 mm |
960 °C 960 °C |
IEC 60695-2-12 | ||
| Oxygen Index | 29 % | |||
| Electrical | Nominal Value | Test Method | ||
| Comparative Tracking Index(Solution A) | 600 V | IEC 60112 | ||
| Dielectric Strength(1 mm) | 34 kV/mm | IEC 60243-1 | ||
| Processing | Nominal Value | |||
| Drying Temperature | 80 °C | |||
| Dry Time(with a dehumidified air drying equipment, dew point mini -20°C) |
2 - 4 h | |||
| Suggested Max Moisture | 0.002 | |||
| Rear Temperature | 230 - 235 °C | |||
| Middle Temperature | 235 - 240 °C | |||
| Front Temperature | 235 - 245 °C | |||
| Mold Temperature | 60 - 90 °C | |||