General | |
Form Resin Pellets | |
Filler 10 % Glass Fiber | |
Feature Chlorinated Flame | |
Retardant | |
Uses | Interior Automotive Components |
Physical Nominal Value Test Method | |
Water Absorption at Saturation(23 ºC) 0.14 % ISO 62 | |
Density / Specific Gravity 1.27 g/cm³ ISO 1183 | |
Mold Shrinkage, TD(3.2 mm) 0.3 - 0.5 % ISO 1183 | |
Mold Shrinkage, MD(3.2 mm) 0.4 - 0.8 % ISO 1183 | |
Mechanical Nominal Value Test Method | |
Tensile Modulus 4400 MPa ISO 527-2 | |
Flexural Modulus 3600 MPa ISO 178 | |
Tensile Strength, Break 82 MPa ISO 527-2 | |
C harpy Impact Strength, Unnotched(23 ºC) 50 kJ/m² ISO 179 | |
Elongation at Break 5.0 % ISO 527-2 | |
Flexural Stress 129 MPa ISO 178 | |
C harpy Impact Strength, Notched(23 ºC) 10 kJ/m² ISO 179 | |
Thermal Nominal Value Test Method | |
Deflection Temperature Under Load, Unannealed | |
0.45 MPa 145 °C ISO 75-2/B | |
1.8 MPa 141 °C ISO 75-2/A | |
CLTE, Transverse 0.4E-4 cm/cm/°C ISO 11359-2 | |
CLTE, Flow 0.67E-4 cm/cm/°C ISO 11359-2 | |
Flammability UL 94 | |
0.75 mm V-2 | |
1.5 mm V-0 | |
Electrical Nominal Value Test Method | |
Comparative Tracking Index PLC 3 UL 746 |