Product Description | |||
PBT 4630-104CE is a glass fiber reinforced and flame-retardant injection-molding grade PBT. | |||
General | |||
Form | Resin Pellets | ||
Filler | 30 % Glass Fiber | ||
Physical | Nominal Value | Test Method | |
Density | 1.63 g/cm³ | ISO 1183 | |
Molding Shrinkage, Across Flow | 0.80 - 1.2 % | ISO 294-4 | |
Molding Shrinkage, Flow | 0.20 - 0.50 % | ISO 294-4 | |
Water Absorption, Equilibrium(50% RH;23 °C) | 0.30 % | ISO 62 | |
Mechanical | Nominal Value | Test Method | |
Tensile Stress, Break | 140 MPa | ISO 527-2 | |
Tensile Strain, Break | 2.3 % | ISO 527-2 | |
Flexural Modulus | 8800 MPa | ISO 178 | |
Flexural Stress | 205 MPa | ISO 178 | |
Charpy Notched Impact Strength(23 °C) | 8.0 kJ/m² | ISO 179/1eA | |
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
215 °C 205 °C |
ISO 75-2/B ISO 75-2/A |
|
Melting Temperature(10 °C/min) | 225 °C | ISO 11357-3 | |
Flame Rating(1.5 mm) | V-0 | UL 94 | |
Electrical | Nominal Value | Test Method | |
Surface Resistivity | > 1.0E+13 ohms | IEC 60093 | |
Volume Resistivity | > 1.0E+16 ohms·cm | IEC 60093 | |
Electric Strength(2 mm) | 22 kV/mm | IEC 60243-1 | |
Processing | Nominal Value | ||
Drying Temperature<Injection> | 120 - 140 °C | ||
Drying Time<Injection> | 3.0 - 5.0 hr | ||
Suggested Max Moisture<Injection> | 0.040 % | ||
Processing Temp, Melt<Injection> | 240 - 270 °C | ||
Mold Temperature<Injection> | 40 - 80 °C |