ABS for Light Resistance; Heat Resistance High Impact Resistance Fax Machines Projectors

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: ABS-763
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

ABS FOR Light resistance; Heat resistance High impact resistance Fax machines projectors

Product Description

Product Description
Features: Light resistance; Heat resistance; High impact resistance; 1.5mm V-0; 2.5mm 5VA Applications: Displays; Chassis; Modems; Power Panels; Power Outlets; Car Batteries; Fax machines; projectors; large all-in-ones; coffee    machines; TV front and rear frames and car audio consoles Weather Resistant
General
Form	Resin Pellets
Feature	Outdoor	Good Thermal		High Impact
UL Yellow Card                          E56070-508235
Uses                                                             Light Covers		Printer Parts		Panel
Socket		Printer Chassis		Remote Controls
Physical		Nominal Value		Test Method
Density / Specific Gravity(23 °C)		1.19 g/cm³		ISO 1183
Melt Volume-Flow Rate, MVR(220 °C;10 kg)		25 cm³/10 min		ISO 1133
Molding Shrinkage		0.30 - 0.60 %		ISO 294-4
Mechanical		Nominal Value		Test Method
Tensile Strength, Yield(50 mm/min)		38.0 MPa		ISO 527-2/50
Tensile Strength, Break(50 mm/min)		29.0 MPa		ISO 527-2/50
Tensile Elongation, Break(50 mm/min)		15 %		ISO 527-2/50
Flexural Modulus(2 mm/min)		2000 MPa		ISO 178
Flexural Strength(2 mm/min)		58.0 MPa		ISO 178
C harpy Notched Impact Strength -30 °C 23 °C		12 kJ/m² 23 kJ/m²		ISO 179
Notched Izod Impact -30 °C 23 °C		11 kJ/m² 22 kJ/m²		ISO 180/1A
Thermal                                                                                Nominal Value					Test Method
Deflection Temperature Under Load, Unannealed(1.8 MPa)			86.0 °C		ISO 75-2/A
Deflection Temperature Under Load, Annealed(1.8 MPa)			96.0 °C		ISO 75-2/A
Vicat Softening Temperature
5 kg;50 ºC/hr			96.0 °C		ISO 306/B50
50 ºC/hr;1 kg			103 °C		ISO 306/A50
CLTE, Flow			8.5E-5 cm/cm/°C		ISO 11359-2
Flame Rating 1.5 mm 2.5 mm			V-0 5VA		UL 94
Processing					Nominal Value
Drying Temperature<Injection>					80 - 85 °C
Drying Time<Injection>					2.0 - 4.0 hr
Rear Temperature<Injection>					180 - 210 °C
Middle Temperature<injection>					190 - 220 °C
Front Temperature<Injection>					190 - 220 °C
Mold Temperature<Injection>					40 - 70 °C
Injection Pressure<Injection>					4.90 - 7.85 MPa
Holding Pressure<Injection>					1.96 - 4.90 MPa
Back Pressure<Injection>					0.490 - 0.981 MPa

 

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 