Product Description | |||
POM copolymer Stiff-flowing type with high melt strength; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470 Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm. Ranges of applications: For extrusion blow molding, and for injection molding thick-walled, void-free molded parts. | |||
General | |||
Form | Resin Pellets | ||
Chemical Resistant Fuel Resistant High Melt Stability | |||
Feature Hydrolysis Resistance Solvent Resistant Fda | |||
Alkali Resistant | |||
Uses Thick-walled Parts Blow Molding | |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.41 g/cm³ | ISO 1183 | |
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 0.90 cm³/10 min | ISO 1133 | |
Water Absorption, Saturation(23 °C) | 0.65 % | ISO 62 | |
Water Absorption, Equilibrium(50% RH;23 °C) | 0.20 % | ISO 62 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus | 2800 MPa | ISO 527-2/1A | |
Tensile Stress, Yield | 65.0 MPa | ISO 527-2/1A/50 | |
Tensile Strain, Yield | 9.0 % | ISO 527-2/1A/50 | |
Nominal Tensile Strain at Break | 25 % | ISO 527-2/1A/50 | |
Tensile creep modulus | ISO 899-1 | ||
1 hr | 2400 MPa | ||
1000 hr | 1200 MPa | ||
Charpy Notched Impact Strength | ISO 179 1eA | ||
-30 °C | 8.0 kJ/m² | ||
23 °C | 10 kJ/m² | ||
Charpy Unnotched Impact Strength(-30 °C) | 200 kJ/m² | ISO 179 1eU | |
Charpy Unnotched Impact Strength, Partial Break(23 °C) | 220 kJ/m² | ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed(1.8 MPa) | 97.0 °C | ISO 75-2/A |
Vicat Softening Temperature | 150 °C | ISO 306/B50 |
Melting Point(10 °C/min) | 167 °C | ISO 11357-3 |
CLTE, Flow | 1.3E-4 cm/cm/°C | ISO 11359-2 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+14 ohms | IEC 60093 |
Volume Resistivity | 1.0e+14 ohms·cm | IEC 60093 |
Electric Strength | 28 kV/mm | IEC 60243-1 |
Relative Permittivity 100 Hz 1000000 Hz |
4.00 4.00 |
IEC 60250 |
Dissipation Factor 100 Hz 1000000 Hz |
2.0E-3 5.0E-3 |
IEC 60250 |
Comparative Tracking Index | 600 V | IEC 60112 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 100 - 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.15 % | |
Hopper Temperature<Injection> | 20 - 30 °C | |
Rear Temperature<Injection> | 170 - 180 °C | |
Middle Temperature<injection> | 180 - 190 °C | |
Front Temperature<Injection> | 190 - 200 °C | |
Nozzle Temperature<Injection> | 190 - 210 °C | |
Processing Temp, Melt<Injection> | 190 - 210 °C | |
Mold Temperature<Injection> | 80 - 120 °C | |
Injection Rate<Injection> | Slow-Moderate | |
Back Pressure<Injection> | < 4.00 MPa | |
Feeding Zone Temperature<Injection> | 60 - 80 °C | |
Zone4 temperature<Injection> | 190 - 210 °C | |
Hot Runner Temperature<Injection> | 190 - 210 °C |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |