Nylon 6/6 Resin Containing 30% Glass Fiber 15% PTFE. Added Features of This Wear Resistant

• Feature: Plastics
• CAS No.: 32131-17-2
• Formula: C36h66n6o6
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA66-RFL36
• EINECS: 618-371-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Natural Color
• Place of Origin: Guangdong, China
• Use: Radiator Front Cover.Automotive Parts
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Delivery Time: in 7 Days
• Applications: Demanding Applications in The Automotive, Furnitur
• Glass Fiber: 30%
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Nylon 6/6 resin containing 30% glass fiber 15% PTFE. Added features of this Wear Resistant
   

  

Product Description
LNP LUBRICOMP RFL36 compound is based on Nylon 6/6 resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Wear Resistant.
General
Form		Resin Pellets
Filler		30 % Glass Fiber		15 % PTFE
Feature		Abrasion Resistant		Structural                          Internally Lubricated
UL Yellow Card	E121562-101344610   E207780-101282824   E45329-101344595
Uses	Consumer		Electrical		Building	and Construction
Physical			Nominal Value			Test Method
Wear Factor Washer			12 10^-10 in^5-min/ft-lb-hr			ASTM D3702 Modified: Manual
Dynamic Cof			0.59			ASTM D3702 Modified: Manual
Density / Specific Gravity			1.51 g/cm³			ISO 1183
Water Absorption(24 hrs;23 °C)			1.34 %			ISO 62-1
Moisture Absorption(50% RH;23 °C)			0.46 %			ISO 62
Melt Volume Rate, MVR(MVR at 275°C/5 kg)			15 - 20 cm³/10 min			ISO 1133
Mold Shrinkage, Flow(24 hrs)			0.2 - 0.5 %			ISO 294
Mold Shrinkage, XFlow(24 hrs)			0.8 - 1.2 %			ISO 294

 

Mechanical	Nominal Value	Test Method
Notched Izod Impact Strength(notched;80*10*3;-40 °C 0)12 kJ/m²		ISO 180/1A
Izod Impact, Unnotched(80*10*4;23 °C)                            84 kJ/m²		ISO 180/1U
Unnotched Izod Impact Strength(unnotched;80*10*4;-4074 kJ/m² °C 0)		ISO 180/1U
Izod Impact, Notched(80*10*4;23 °C)                                16 kJ/m²		ISO 180/1A
Tensile Stress, Break(5 mm/min)                                        166 MPa		ISO 527
Tensile Strain, Break(5 mm/min)                                        2.6 %		ISO 527
Flexural Stress, Yield 2 mm/min 2 mm/min;60°C 2 mm/min;100 °C 2 mm/min;150°C 2 mm/min;200°C	234 MPa 179 MPa 131 MPa 96 MPa 83 MPa	ISO 178
Flexural Stress, break(2 mm/min)                                       277 MPa		ISO 178
Flexural Strain, Break 2 mm/min 2 mm/min;60°C 2 mm/min;100 °C 2 mm/min;150°C 2 mm/min;200°C	4.1 % 6.1 % 6.6 % 5.6 % 6.3 %	ISO 178
Flexural Modulus 2 mm/min 2 mm/min;60°C 2 mm/min;100 °C 2 mm/min;150°C 2 mm/min;200°C	9100 MPa 5300 MPa 4200 MPa 3500 MPa 3100 MPa	ISO 178

 

Thermal	Nominal Value	Test Method
UL Recognized(≥ 0.75 mm)	HB	UL 94
Specific Heat	1988 J/kg-K	ASTM E1269
CTE, Flow(23°C to 60°C)	2.5e-05 1/°C	ISO 11359-2
CTE, XFlow(23°C to 60°C)	7.5e-05 1/°C	ISO 11359-2
HDT/Bf(0.45)	> 220 °C	ISO 75/Bf
HDT/Af(1.8)	> 220 °C	ISO 75/Af
Thermal Conductivity	0.25 W/m-K	ASTM D5930
Relative Temp Index, Elec	120 °C	UL 746B
Relative Temp Index, Mechanical with Impact	65 °C	UL 746B
Relative Temp Index, Mechanical without Impact	65 °C	UL 746B
Processing		Nominal Value
Drying Temperature<Injection>		80 °C
Drying Time<Injection>		4 hrs
Maximum Moisture Content<Injection>		0.15 - 0.25 %
Melt Temperature<Injection>		280 - 305 °C
Front, Zone 3 Temperature<Injection>		295 - 305 °C
Middle, Zone 2 Temperature<Injection>		280 - 295 °C
Rear, Zone 1 Temperature<Injection>		265 - 275 °C
Mold Temperature<Injection>		95 - 110 °C
Back Pressure<Injection>		0.2 - 0.3 MPa
Screw Speed<Injection>		30 - 60 rpm

  

Company Profile

Product Parameters

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry