PC 1261-03 resin is designed for extrusion blow molding(EBM) and injection stretch blow molding(ISBM) products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. Two base colors available: Ultra blue B0786T & Ice blue W0992T | |||
General | |||
Form | Resin Pellets | ||
High Viscosity Fda Eu Food Contact | |||
Good Thermal | |||
c eac | nese an ar | ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 2.5 g/10min | ASTM D1238 | |
Molding Shrinkage, Flow | 0.50 - 0.70 % | ASTM D955 | |
Water Absorption(24 hr;23 °C) | 0.15 % | ASTM D570 | |
Water Absorption, Equilibrium(50% RH;23 °C) | 0.32 % | ASTM D570 | |
Rockwell Hardness, M-Scale | 74 | ASTM D785 | |
Rockwell Hardness, R-Scale | 118 | ASTM D785 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus | 2410 MPa | ASTM D638 | |
Tensile Strength, Yield | 60.0 MPa | ASTM D638 | |
Tensile Strength, Break | 72.0 MPa | ASTM D638 | |
Tensile Elongation, Yield | 6.0 % | ASTM D638 | |
Tensile Elongation, Break | 150 % | ASTM D638 | |
Flexural Modulus | 2410 MPa | ASTM D790 | |
Flexural Strength | 96.0 MPa | ASTM D790 | |
Taber Abrasion Resistance - Change in Haze(1000g;CS- 10F Wheel;500 Cycles) | 45 % | ASTM D1044 | |
Notched Izod Impact(23 °C) | 950 J/m | ASTM D256 | |
Unnotched Izod Impact(23 °C) | No Break | ASTM D256 | |
Instrumented Dart Impact, Total Energy(23 °C) | 94.0 J | ASTM D3763 | |
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Annealed 0.45 MPa;4 mm 1.8 MPa;4 mm |
146 °C 143 °C |
ASTM D648 | |
Deflection Temperature Under Load, Unannealed(1.8 MPa;4 mm) | 132 °C | ASTM D648 | |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 151 °C | ASTM D1525 | |
Ball Indentation Temperature | > 125 °C | IEC 60598-1 | |
CLTE, Flow(-40 - 82 °C) | 6.8E-5 cm/cm/°C | ASTM D696 | |
Glow Wire Ignition Temperature [GWIT](2 mm;5 sec) | 850 °C | IEC 60695-2-13 | |
Oxygen Index | 26 % | ASTM D2863 | |
Average Extent of Burning | 3 cm | ASTM D635 | |
Electrical | Nominal Value | Test Method | |
Volume Resistivity(23 °C) | 2.0E+17 ohms ·cm | ASTM D257 | |
Dielectric Strength | 17 kV/mm | ASTM D149 | |
Dielectric Constant(60 Hz) | 3.00 | ASTM D150 | |
Dissipation Factor(60 Hz) | 1.0E-3 | ASTM D150 | |
Comparative Tracking Index(2 mm) | 250 V | IEC 60112 | |
Optical | Nominal Value | Test Method | |
Refractive Index | 1.586 | ASTM D542 | |
Transmittance | 89.0 % | ASTM D1003 | |
Haze | 0.700 - 1.50 % | ASTM D1003 |