| Feature: | Plastics |
|---|---|
| CAS No.: | 25766-59-0 |
| Formula: | C6h4c(CH3)2c6h4oco2-]N |
| Samples: |
25kg/bag
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier | Product Description | ||||||||||
| UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 10.5 MFR. UV- stabilized. Internal mold release. | ||||||||||
| General | ||||||||||
| Form | Resin Pellets | |||||||||
| Feature | Outdoor | F1 | Non-Brominated & Non- Chlorinated Flame Retardant |
|||||||
| UL Yellow Card | E207780-100738000 | |||||||||
| Appliances Lighting Applications Automotive Lighting | ||||||||||
| Hood Encapsulation | ||||||||||
| Electronic Displays Lawn And Garden | Packaging | |||||||||
| qu pmen Pharmaceuticals | ||||||||||
| Uses Sporting Goods Textile Applications Aerospace | ||||||||||
| Constraction Household Applications Outdoor | ||||||||||
| Rail Electrical Medical |
||||||||||
| Non-specific Food | ||||||||||
| Applications | ||||||||||
| Physical Nominal Value Test Method | ||||||||||
| Density / Specific Gravity 1.19 - 1.20 g/cm³ ASTM D792 | ||||||||||
| Specific Volume 0.830 cm³/g ASTM D792 | ||||||||||
| Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) 11 g/10min ASTM D1238 | ||||||||||
| Molding Shrinkage, Flow(3.2 mm) 0.50 - 0.70 % Internal Method | ||||||||||
| Water Absorption(24 hr) 0.15 % ASTM D570 | ||||||||||
| Water Absorption, Equilibrium ASTM D570 | ||||||||||
| 23 °C 0.35 % | ||||||||||
| 100 °C 0.58 % | ||||||||||
| Outdoor Suitability f1 UL 746C | ||||||||||
| Rockwell Hardness, M-Scale 70 ASTM D785 | ||||||||||
| Rockwell Hardness, R-Scale 118 ASTM D785 | ||||||||||
| Mechanical Nominal Value | Test Method | |||||||||
| Tensile Strength, Yield(50 mm/min;Type I) 62.0 MPa | ASTM D638 | |||||||||
| Tensile Strength, Break(50 mm/min;Type I) 65.0 MPa | ASTM D638 | |||||||||
| Tensile Elongation, Yield(50 mm/min;Type I) 7.0 % | ASTM D638 | |||||||||
| Tensile Elongation, Break(50 mm/min;Type I) 110 % | ASTM D638 | |||||||||
| Flexural Modulus(1.3 mm/min;50 mm;Span) 2340 MPa | ASTM D790 | |||||||||
| Flexural Strength, Yield(1.3 mm/min;50 mm;Span) 93.0 MPa | ASTM D790 | |||||||||
| Taber Abrasion Resistance(1.0e+3 Cycles;1.0e+3 g;CS-1710.0 mg Wheel) |
ASTM D1044 | |||||||||
| Notched Izod Impact(23 °C) 800 J/m | ASTM D256 | |||||||||
| Unnotched Izod Impact(23 °C) 3200 J/m | ASTM D4812 | |||||||||
| Gardner Impact(23 °C) 169 J | ASTM D3029 | |||||||||
| Tensile Impact Strength(Type S) 546 kJ/m² | ASTM D1822 | |||||||||
| Thermal Nominal Value | Test Method | |||||||||
| Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;6.4 mm |
137 °C 132 °C |
ASTM D648 | ||||||||
| Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 154 °C | ASTM D1525 | ||||||||
| CLTE, Flow(-40 - 95 °C) 6.8E-5 cm/cm/°C | ASTM E831 | |||||||||
| Specific Heat 1250 J/kg/°C | ASTM C351 | |||||||||
| Thermal Conductivity 0.19 W/m-K | ASTM C177 | |||||||||
| RTI Elec 130 °C | UL 746 | |||||||||
| RTI Imp 130 °C | UL 746 | |||||||||
| RTI Str 130 °C | UL 746 | |||||||||
| Flame Rating(0.76 mm) HB | UL 94 | |||||||||
| Oxygen Index 25 % | ASTM D2863 | |||||||||
| Electrical | Nominal Value | Test Method | ||||||||
| Volume Resistivity | > 1.0E+17 ohms ·cm | ASTM D257 | ||||||||
| Dielectric Strength, in Air(3.2 mm) | 15 kV/mm | ASTM D149 | ||||||||
| Dielectric Constant 60 Hz 5.0e+4 Hz 1.0e+6 Hz |
3.17 3.17 2.96 |
ASTM D150 | ||||||||
| Dissipation Factor 50 Hz 60 Hz 1.0e+6 Hz |
9.0E-4 9.0E-4 0.010 |
ASTM D150 | ||||||||
| Comparative Tracking Index, CTI | PLC 2 | UL 746 | ||||||||
| High Amp Arc Ignition, HAI, Surface | PLC 1 | UL 746 | ||||||||
| High Voltage Arc Tracking Rate, HVTR | PLC 2 | UL 746 | ||||||||
| Hot-wire Ignition, HWI | PLC4 | UL 746 | ||||||||
| Optical | Nominal Value | Test Method | ||||||||
| Refractive Index | 1.586 | ASTM D542 | ||||||||
| Transmittance (2.5e+3 µm) | 88.0 % | ASTM D1003 | ||||||||
| Haze(2.5e+3 µm) | 1.00 % | ASTM D1003 | ||||||||
| Processing | Nominal Value | |||||||||
| Drying Temperature<Injection> | 120 °C | |||||||||
| Drying Time<Injection> | 3.0 - 4.0 hr | |||||||||
| Suggested Max Moisture<Injection> | 0.020 % | |||||||||
| Suggested Shot Size<Injection> | 40 - 60 % | |||||||||
| Rear Temperature<Injection> | 270 - 295 °C | |||||||||
| Middle Temperature<injection> | 280 - 305 °C | |||||||||
| Front Temperature<Injection> | 295 - 315 °C | |||||||||
| Nozzle Temperature<Injection> | 290 - 310 °C | |||||||||
| Processing Temp, Melt<Injection> | 295 - 315 °C | |||||||||
| Mold Temperature<Injection> | 70 - 95 °C | |||||||||
| Back Pressure<Injection> | 0.300 - 0.700 MPa | |||||||||
| Screw Speed <Injection> | 40 - 70 rpm | |||||||||
| Vent Depth <Injection> | 0.025 - 0.076 mm | |||||||||
| Drying Time, Cumulative<Injection> | 48 hrs | |||||||||