Nylon 6 resin containing mineral and glass fiber Added features of this grade include
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | ||||
LNP KONDUIT PX11311 compound is based on Nylon 6 resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative and Non-Brominated, Non-Chlorinated Flame Retardant. | ||||
General | ||||
Form | Resin Pellets | |||
Filler | Glass Fiber | Mineral | ||
Feature |
Thermally Conductive | Non-Brominated & Non- Chlorinated Flame Retardant |
Non-Chlorinated Electrically Isolative |
|
UL Yellow Card E207780-101041511 | ||||
Uses | Consumer Industria Building and Construction | Electrical | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.74 g/cm³ | ASTM D792 | ||
Mold Shrinkage, Flow(24 hrs) | 0.33 % | ASTM D955 | ||
Mold Shrinkage, XFlow(24 hrs) | 0.48 % | ASTM D955 | ||
Water Absorption(24 hrs;23 °C) | 0.25 % | Method | ||
Moisture Absorption(50% RH;23 °C) | 0.04 % | ISO 62 | ||
Melt Volume Rate, MVR(10 kg;MVR at 300 °C) | 49 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Unnotched(23 °C) | 183 J/m | ASTM D4812 | ||
Izod Impact, Notched(23 °C) | 43 J/m | ASTM D256 | ||
Tensile Stress, Break(5 mm/min;Type I) | 52 MPa | ASTM D638 | ||
Tensile Strain, Break(5 mm/min;Type I) | 2 % | ASTM D638 | ||
Tensile Modulus(5 mm/min) | 7240 MPa | ASTM D638 | ||
Flexural Stress, break(1.3 mm/min;50 mm;span) | 76 MPa | ASTM D790 | ||
Flexural Modulus(1.3 mm/min;50 mm;span) | 9040 MPa | ASTM D790 | ||
Impact Strength | 5.3 - 18.2 kJ/m² | ISO R179 | ||
Thermal | Nominal Value | Test Method | ||
UL Recognized(≥ 1 mm) | V-0 | UL 94 | ||
Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm |
775 °C 850 °C |
IEC 60695-2-13 | ||
Glow Wire Flammability Index 3 mm 1 mm |
960 °C 960 °C |
IEC 60695-2-12 | ||
Heat Deflection Temperature[HDT], Unannealed(1.82 MPa;6.4 mm) | 199 °C | ASTM D648 | ||
CTE, Flow -40 - 40 °C 40°C to 120°C |
3.1E-05 1/°C 1.9E-05 1/°C |
ASTM E831 | ||
CTE, XFlow -40 - 40 °C 40°C to 120°C |
4.6E-05 1/°C 6.9e-05 1/°C |
ASTM E831 | ||
Specific Heat | 1.42 J/g-°C | ASTM C351 | ||
Thermal conductivity through plane 10*10*3mm sample ?80*3mm discs |
1.2 W/m-K 0.99 W/m-K |
ASTM E1461-07 ISO 22007-2 |
||
Thermal conductivity in plane 25*0.4mm disc ?80*3mm discs |
2.1 W/m-K 1.38 W/m-K |
ASTM E1461-07 ISO 22007-2 |
||
Relative Temp Index, Elec | 65 °C | UL 746B | ||
Relative Temp Index, Mechanical with Impact | 65 °C | UL 746B | ||
Relative Temp Index, Mechanical without Impact | 65 °C | UL 746B | ||
Electrical | Nominal Value | Test Method | ||
Surface Resistivity | > 1.E+15 ohms | ASTM D257 | ||
Dielectric Strength, in Oil(1 mm) | > 10 kV/mm | ASTM D149 | ||
Dielectric Constant, Dk(1.1e+9 Hz) | 4.74 | ASTM ES 7-83 | ||
Dissipation Factor, Df(1.1e+9 Hz) | 7.7E-03 | ASTM ES 7-83 | ||
Comparative Tracking Index | 600 V | IEC 60112 | ||
Comparative Tracking Index, CTI | PLC 0 | UL 746A | ||
Hot-wire Ignition, HWI ≥ 3 mm ≥ 1 mm |
PLC 0 PLC 2 |
UL 746A | ||
High Amp Arc Ignition, HAI( ≥ 1 mm) | PLC 0 | UL 746A | ||
Processing | Nominal Value | |||
Drying Temperature<Injection> | 80 °C | |||
Drying Time<Injection> | 4 hrs | |||
Maximum Moisture Content<Injection> | 0.15 - 0.25 % | |||
Melt Temperature<Injection> | 270 - 295 °C | |||
Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |||
Middle, Zone 2 Temperature<Injection> | 270 - 290 °C | |||
Rear, Zone 1 Temperature<Injection> | 260 - 275 °C | |||
Mold Temperature<Injection> | 85 - 100 °C | |||
Back Pressure<Injection> | 0.2 - 0.3 MPa | |||
Screw Speed <Injection> | 20 - 60 rpm |