Flame retardant Black color LDS Laser Direct Structuring polycarbonate Red Phosphorous Freee
https://forever-plastics.en.made-in-china.com/product-list-1.html
Product Description | ||||
LDS (Laser Direct Structuring), Flame retardant (Non Br & Non P), Black color only | ||||
General | ||||
Form | Resin Pellets | |||
Filler | Proprietary Filler | |||
Feature | Lds Laser Markable |
Non-Brominated Red Phosphorous Free | ||
UL Yellow Card | E340159-100746645 | |||
Uses Laser Direct Structuring | Cell Phone Cases | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.26 g/cm³ | ISO 1183 | ||
Melt Mass-Flow Rate, MFR(260 °C;5 kg) | 8.0 g/10min | ISO 1133 | ||
Melt Volume-Flow Rate, MVR(260 °C;5 kg) | 8.00 cm³/10 min | ISO 1133 | ||
Molding Shrinkage, Across Flow | 0.40 - 0.60 % | Internal Method | ||
Molding Shrinkage, Flow | 0.40 - 0.60 % | Internal Method | ||
Water Absorption, Saturation(23 °C) | 0.35 % | ISO 62 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus | 2200 MPa | ISO 527-2/1 | ||
Tensile Stress, Yield | 52.0 MPa | ISO 527-2/50 | ||
Tensile Strain, Yield | 5.0 % | ISO 527-2/50 | ||
Tensile Strain, Break | > 50 % | ISO 527-2/50 | ||
Flexural Modulus(2 mm/min) | 2300 MPa | ISO 178 | ||
Flexural Stress(2 mm/min) | 80.0 MPa | ISO 178 | ||
C harpy Notched Impact Strength -30 °C 23 °C |
30 kJ/m² 55 kJ/m² |
ISO 179 | ||
C harpy Unnotched Impact Strength -30 °C 23 °C |
No Break No Break |
ISO 179 | ||
Notched Izod Impact Strength -20 °C 23 °C |
40 kJ/m² 60 kJ/m² |
ISO 180/4A | ||
Multi-Axial Instrumented Impact Energy(23 °C) | 35.0 J | ISO 6603-2 | ||
Thermal | Nominal Value | Test Method | ||
Heat Deflection Temperature, Unannealed(1.8 MPa) | 122 °C | ISO 75-2/A | ||
Vicat Softening Temperature | 144 °C | ISO 306 | ||
CLTE, Flow | 6.0E-5 cm/cm/°C | ISO 11359-2 | ||
CLTE, Transverse | 6.5E-5 cm/cm/°C | ISO 11359-2 | ||
Flame Rating 0.5 mm 1.5 mm 3 mm |
HB V-0 5VB |
UL 94 | ||
Electrical | Nominal Value | Test Method | ||
Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 | ||
Volume Resistivity | > 1.0E+15 Ohms ·cm | IEC 60093 | ||
Dielectric Constant(1.0e+6 Hz) | 3.00 | IEC 60250 | ||
Dissipation Factor(1.0e+6 Hz) | 5.0E-3 | IEC 60250 | ||
Processing | Nominal Value | |||
Drying Temperature - Hot Air Dryer<Injection> | 100 - 120 °C | |||
Drying Time - Hot Air Dryer<Injection> | 4.0 - 6.0 hr | |||
Rear Temperature<Injection> | 270 - 300 °C | |||
Middle Temperature<injection> | 270 - 300 °C | |||
Front Temperature<Injection> | 270 - 300 °C | |||
Nozzle Temperature<Injection> | 270 - 300 °C | |||
Mold Temperature<Injection> | 80 - 120 °C |