Feature: | Plastics |
---|---|
CAS No.: | 63440-93-7 |
Formula: | C24h24o8 |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
General |
||||
Form |
Resin Pellets |
|||
Feature |
35 % Pcr |
Non-Brominated & Non- Chlorinated Flame Retardant |
Non-Chlorinated Pcr |
|
Usage Electrical |
||||
Physical |
Nominal Value |
Test Method |
||
Density / Specific Gravity |
1.18 |
ASTM D792 |
||
Water Absorption(24 hrs;23 °C) |
0.1 % |
ASTM D570 |
||
Melt Flow Rate[MFR](260 °C;2.16 kgf) |
21 g/10min |
ASTM D1238 |
||
Mechanical |
Nominal Value |
Test Method |
||
Izod Impact, Notched(23 °C) |
500 J/m |
ASTM D256 |
||
Instrumented Dart Impact, Total Energy(23 °C) |
50 J |
ASTM D3763 |
||
Notched Izod Impact Strength(notched;80*10*3;23 °C 0) |
51 kJ/m² |
ISO 180/1A |
||
Tensile Stress, Yield(50 mm/min;Type I) |
60 MPa |
ASTM D638 |
||
Tensile Stress, Break(50 mm/min;Type I) |
47 MPa |
ASTM D638 |
||
Tensile Strain, Yield(50 mm/min;Type I) |
4 % |
ASTM D638 |
||
Tensile Strain, Break(50 mm/min;Type I) |
40 % |
ASTM D638 |
||
Tensile Modulus(50 mm/min) |
2500 MPa |
ASTM D638 |
||
Flexural Stress, Yield(1.3 mm/min;50 mm;span) |
90 MPa |
ASTM D790 |
||
Flexural Modulus(1.3 mm/min;50 mm;span) |
2400 MPa |
ASTM D790 |
Thermal |
Nominal Value |
Test Method |
UL Recognized ≥ 1.5 mm ≥ 1.2 mm ≥ 0.3 mm |
V-0 V-1 HB |
UL 94 |
Vicat Softening Temperature(Rate B/50) |
100 °C |
ASTM D1525 |
Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 0.45 MPa;6.4 mm 1.82 MPa;6.4 mm |
85 °C 101 °C 92 °C |
ASTM D648 |
CTE, Flow(-40°C to 60°C) |
7.1e-05 1/°C |
ASTM E831 |
CTE, XFlow(-40°C to 60°C) |
7.2e-05 1/°C |
ASTM E831 |
Relative Temp Index, Elec |
85 °C |
UL 746B |
Relative Temp Index, Mechanical with Impact |
85 °C |
UL 746B |
Relative Temp Index, Mechanical without Impact |
85 °C |
UL 746B |
Electrical |
Nominal Value |
Test Method |
Hot-wire Ignition, HWI( ≥ 3 mm) |
PLC 2 |
UL 746A |
Processing |
Nominal Value |
|
Drying Temperature<Injection> |
80 - 90 °C |
|
Drying Time<Injection> |
3 - 4 hrs |
|
Drying Time, Cumulative<Injection> |
8 hrs |
|
Maximum Moisture Content<Injection> |
0.04 % |
|
Melt Temperature<Injection> |
245 - 275 °C |
|
Nozzle Temperature<Injection> |
245 - 275 °C |
|
Front, Zone 3 Temperature<Injection> |
245 - 275 °C |
|
Middle, Zone 2 Temperature<Injection> |
220 - 265 °C |
|
Rear, Zone 1 Temperature<Injection> |
220 - 255 °C |
|
Mold Temperature<Injection> |
60 - 80 °C |
|
Back Pressure<Injection> |
0.3 - 0.7 MPa |
|
Screw Speed <Injection> |
40 - 70 rpm |
|
Shot To Cylinder Size<Injection> |
30 - 80 % |
|
Vent Depth <Injection> |
0.038 - 0.076 mm |