Polycarbonate (PC) Is an Injection Moldable Non-Chlorinated/Brominated Flame Retardant Grade

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC-505RU
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Polycarbonate (PC) is an injection moldable non-chlorinated/brominated flame retardant grade

Product Description

 

Product Description
505RU Polycarbonate (PC) is an injection moldable non-chlorinated/brominated flame retardant grade that is 10% glass fiber filled. It It is UV stabilized and has a UL94 [email protected] rating and is available in various   opaque color options. This is an alternative to 503R, 503R, 503RS.
General
Form		Resin Pellets
Filler		10 % Glass Fiber
Feature		Outdoor                            F1 Non-Chlorinated			Non-Brominated
UL Yellow Card                         E207780-100059995
Uses	Appliances   Energy Storage		Lighting Applications       Electronic Displays
Physical			Nominal Value			Test Method
Density / Specific Gravity			1.26 g/cm³			ASTM D792;ISO 1183
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg)			8.0 g/10min			ASTM D1238
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg)			7.00 cm³/10 min			ISO 1133
Molding Shrinkage, Flow(3.2 mm)			0.40 - 0.60 %			Internal Method
Water Absorption, Saturation(23 °C)			0.30 %			ISO 62
Water Absorption, Equilibrium(50% RH;23 °C)			0.15 %			ISO 62
Outdoor Suitability			f1			UL 746C
Mechanical			Nominal Value			Test Method
Tensile Modulus
5 mm/min			3600 MPa			ASTM D638
			3500 MPa			ISO 527-2/1
Tensile Strength, Yield
5 mm/min;Type I			74.0 MPa			ASTM D638
			72.0 MPa			ISO 527-2/5
Tensile Strength, Break
5 mm/min;Type I			62.0 MPa			ASTM D638
			60.0 MPa			ISO 527-2/5
Tensile Elongation, Yield
5 mm/min;Type I			4.0 %			ASTM D638
			3.0 %			ISO 527-2/5
Tensile Elongation, Break 5 mm/min;Type I			6.0 % 6.0 %			ASTM D638 ISO 527-2/5
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min			3200 MPa 3500 MPa			ASTM D790 ISO 178
Flexural Stress, at Yield(2 mm/min)			122 MPa			ISO 178
Flexural Stress, Yield(1.3 mm/min;50 mm;Span)			114 MPa			ASTM D790
C harpy Notched Impact Strength -30 °C;80 23 °C;80			7.0 kJ/m² 10 kJ/m²			ISO 179 1eA
C harpy Unnotched Impact Strength -30 °C;80 23 °C;80			No Break No Break			ISO 179 1eU
Notched Izod Impact -30 °C 23 °C -30 °C;80*10*3 mm 23 °C;80*10*3 mm			70 J/m 90 J/m 8.0 kJ/m² 10 kJ/m²			ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A
Unnotched Izod Impact 23 °C -30 °C;80*10*3 mm 23 °C;80*10*3 mm			1200 J/m 73 kJ/m² No Break			ASTM D4812 ISO 180/1U   ISO 180/1U
Instrumented Dart Impact, Total Energy(23 °C)			25.0 J			ASTM D3763
Thermal			Nominal Value			Test Method
Deflection Temperature Under Load, Unannealed
1.8 MPa;3.2 mm			137 °C			ASTM D648
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span			136 °C			ASTM D1525
Vicat Softening Temperature
50 °C/h;50 N;Rate A;Loading 2			149 °C 147 °C			ISO 306 ISO 306/B50
Ball Pressure Test(123 - 127 °C)			Pass			ISO 11359-2
CLTE, Flow(-40 - 40 °C)			5.0E-5 cm/cm/°C			ASTM E831
CLTE, Transverse
-40 - 40 °C			7.4E-5 cm/cm/°C			ASTM E831
-40 °C			8.5E-5 cm/cm/°C			ISO 11359-2
Flame Rating, Testing  0.75 mm 1.5 mm 3 mm 3 mm			V-2 V-0 5VA 5VB			UL 94
Glow Wire Flammability Index(0.75 mm)			960 °C			IEC 60695-2-12
Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm			850 °C 875 °C			IEC 60695-2-13
Electrical			Nominal Value			Test Method
Comparative Tracking Index[CTI]			PLC 3			UL 746
Comparative Tracking Index			175 V			IEC 60112
High Amp Arc Ignition, HAI, Surface			PLC 0			UL 746
Hot-wire Ignition, HWI			PLC 3			UL 746
Processing				Nominal Value
Drying Temperature<Injection>				120 °C
Drying Time<Injection>				2.0 - 4.0 hr
Suggested Max Moisture<Injection>				0.020 %
Hopper Temperature<Injection>				60 - 80 °C
Rear Temperature<Injection>				270 - 300 °C
Middle Temperature<injection>				280 - 310 °C
Front Temperature<Injection>				290 - 320 °C
Nozzle Temperature<Injection>				280 - 310 °C
Processing Temp, Melt<Injection>				290 - 320 °C
Mold Temperature<Injection>				80 - 120 °C

 
 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....