Feature: | Oxidative Degradable |
---|---|
CAS No.: | 32131-17-2 |
Formula: | (C12h22n2o2)N |
Samples: |
BAG
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
PA66 grade solenoid valve housings electrical flow heaters Polyamine Nylon 66
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | ||||
A3HG7 is a 35% glass fiber reinforced injection molding PA66 grade. Applications Typical applications include machinery components and housings of high stiffness and dimensional stability such as gears, solenoid valve housings, electrical flow heaters, trailing cable attachments, as well as electrically insulating parts. | ||||
General | ||||
Form | Resin Pellets | |||
Filler | 35 % Glass Fiber | |||
Feature | Good Dimensional Ec 1907/2006 (Reach) |
Good Hardness | Fuel Resistant | |
UL Yellow Card E41871-233736 | ||||
Uses | Electronic Insulation Mechanical Parts | Gear Wheels Housing | ||
Physical | Nominal Value | Test Method | ||
Density, dry | 1.41 g/cm³ | ISO 1183 | ||
Dry: Melt Volume-Flow Rate, MVR(275 °C;5 kg) | 40 cm³/10 min | ISO 1133 | ||
Dry: Water Absorption, Saturation(23 °C) | 5.0 % | ISO 62 | ||
Dry: Water Absorption, Equilibrium(50% RH;23 °C) | 1.6 % | ISO 62 | ||
Mechanical | Nominal Value | Test Method | ||
Dry: Tensile Modulus(23 °C) | 11500 MPa | ISO 527-2 | ||
Condition: Tensile Modulus(23 °C) | 8500 MPa | ISO 527-2 | ||
Dry: Tensile Stress, Break(23 °C) | 210 MPa | ISO 527-2 | ||
Condition: Tensile Stress, Break(23 °C) | 150 MPa | ISO 527-2 | ||
Dry: Tensile Strain, Break(23 °C) | 3.0 % | ISO 527-2 | ||
Condition: Tensile Strain, Break(23 °C) | 5.0 % | ISO 527-2 | ||
Dry: Flexural Modulus(23 °C) | 10000 MPa | ISO 178 | ||
Dry: Charpy Notched Impact Strength | ISO 179 | |||
-30 °C | 12 kJ/m² | |||
23 °C | 13 kJ/m² | |||
Condition: Charpy Notched Impact Strength(23 °C) | 22 kJ/m² | ISO 179 | ||
Dry: Charpy Unnotched Impact Strength | ISO 179 | |||
-30 °C | 75 kJ/m² | |||
23 °C | 95 kJ/m² | |||
Condition: Charpy Unnotched Impact Strength(23 °C) | 110 kJ/m² | ISO 179 | ||
Thermal | Nominal Value | Test Method | ||
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
250 °C 250 °C |
ISO 75-2/B ISO 75-2/A |
||
Dry: Melting Temperature, DSC | 260 °C | ISO 3146 | ||
Dry: CLTE, Flow | 1.7E-5 cm/cm/°C | No Standard | ||
Dry: CLTE, Transverse | 6.5E-5 cm/cm/°C | No Standard | ||
Dry: RTI Elec 0.8 mm 1.5 mm 3 mm |
120 °C 120 °C 120 °C |
UL 746 | ||
Dry: RTI Imp 1.5 mm 3 mm |
120 °C 120 °C |
UL 746 | ||
Dry: RTI Str 1.5 mm 3 mm |
130 °C 130 °C |
UL 746 | ||
Dry: Flame Rating 0.8 mm 1.5 mm 3 mm |
HB HB HB |
UL 94 | ||
Electrical | Nominal Value | Test Method | ||
Dry: Volume Resistivity | 1.0e+17 ohms ·cm | IEC 60093 | ||
Condition: Volume resistivity | 1.0E+12 ohms ·cm | IEC 60093 | ||
Dry: Dielectric Constant(1.0e+6 Hz) | 3.50 | IEC 60250 | ||
Condition: Dielectric Constant(1.0e+6 Hz) | 5.70 | IEC 60250 | ||
Dry: Dissipation Factor 100 Hz 1.0e+6 Hz |
0.020 0.020 |
IEC 60250 | ||
Condition: Dissipation factor 100 Hz 1.0e+6 Hz |
0.30 0.15 |
IEC 60250 | ||
Dry: Comparative Tracking Index | 550 V | IEC 60112 | ||
Condition: Comparative Tracking Index | 550 V | IEC 60112 | ||
Processing | Nominal Value | |||
Drying Temperature<Injection> | 80 °C | |||
Drying Time<Injection> | 2.0 - 4.0 hr | |||
Suggested Max Moisture<Injection> | 0.12 % | |||
Processing Temp, Melt<Injection> | 280 - 305 °C | |||
Mold Temperature<Injection> | 80 - 90 °C | |||
Injection Pressure<Injection> | 3.50 - 12.5 MPa | |||
Injection Rate<Injection> | Fast |