Product Description |
RKN14 compound is based on Nylon 6/6 resin containing 20% mineral and Molybdenum diSulfide (MoS2). Added features of this grade include: Dimensional Control, Wear Resistant |
General |
Form Resin Pellets |
Filler 20 % Mineral MoS2 |
Feature Good Dimensional Abrasion Resistant Internally Lubricated |
Uses Consumer Electrical Building and Construction |
Physical Nominal Value Test Method |
Molding Shrinkage, Flow, Tensile Bar 0.7 - 0.9 % Method |
Density / Specific Gravity 1.34 g/cm³ ISO 1183 |
Mechanical Nominal Value Test Method |
Izod Impact, Unnotched(80*10*4;23 °C) 50 kJ/m² ISO 180/1U |
Izod Impact, Notched(80*10*4;23 °C) 6 kJ/m² ISO 180/1A |
Tensile Stress, Break(5 mm/min) 77 MPa ISO 527 |
Tensile Strain, Break(5 mm/min) 4.2 % ISO 527 |
Tensile Modulus(1 mm/min) 6300 MPa ISO 527 |
Flexural Stress, break(2 mm/min) 111 MPa ISO 178 |
Flexural Modulus(2 mm/min) 5000 MPa ISO 178 |
Thermal Nominal Value Test Method |
HDT/Af(1.8) 104 °C ISO 75/Af |
Processing Nominal Value |
Back Pressure<Injection> 0.2 - 0.3 MPa |
Drying Temperature<Injection> 120 °C |
Drying Time<Injection> 4 hrs |
Front, Zone 3 Temperature<Injection> 295 - 305 °C |
Maximum Moisture Content<Injection> 0.15 - 0.25 % |
Melt Temperature<Injection> 275 - 290 °C |
Middle, Zone 2 Temperature<Injection> 280 - 295 °C |
Mold Temperature<Injection> 80 - 95 °C |
Rear, Zone 1 Temperature<Injection> 265 - 275 °C |
Screw Speed <Injection> 30 - 60 rpm |