Resins Be Dried Prior to Molding Information Provided by Solvay Specialty Polymers

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PPA-HFZ-A1133L
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide
 Heat-conducting nylon

Product Description

Product Description
HFZ A-1133 L is a high-flow, 33% glass fiber reinforced polyphthalamide (PPA) grade.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Flow; High Stiffness; High Strength; High Temperature Strength Uses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Bobbins; Connectors; Electrical/Electronic Applications; General Purpose; Industrial Applications; Industrial Parts; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal ReplacementInjection Molding Notes: compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122° F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that  resins be dried prior to molding.Information provided by Solvay Specialty Polymers
General
Form                                        Resin Pellets
Filler                                         33 % Glass Fiber
Physical	Nominal Value	Test Method
Density / Specific Gravity	1.49 g/cm³	ISO 1183
Filler Content(Glass Fiber)	33 %
Mechanical	Nominal Value	Test Method
Tensile Strength, Break	188 MPa	ISO 527-2
Elongation at Break	1.7 %	ISO 527-2
Tensile Modulus	1.12E+4 MPa	ISO 527-2
Flexural Strength	268 MPa	ISO 178
Flexural Modulus	1.04E+4 MPa	ISO 178
Izod Impact, Notched, ISO(Temperature; 23 °C)	10.0 kJ/m²	ISO 180
C harpy Impact, Notched(Temperature; 23 °C)	8.2 kJ/m²	ISO 179
Thermal	Nominal Value	Test Method
Deflection Temperature(Pressure; 1.8 MPa;flatwise)	296 °C	ISO 75-2/A
Processing		Nominal Value
Rear Barrel Temperature		316 - 329 °C
Middle Barrel Temperature		316 - 329 °C
Front Barrel Temperature		324 - 335 °C
Melt Temperature		321 - 345 °C
Mold Temperature		150 °C
Drying Temperature(Time 4 hr)		120 °C
Moisture Content		0.030 - 0.060 %

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 