ABS FOR projectors large MFPs coffee makers TV front and rear frames and car audio consoles
https://forever-plastics.en.made-in-china.com/product-list-1.html
Product Description | |||||
Features: High Flow; 1.5mm V-1; 2.1mm V-0; 2.1mm 5VB; 2.5mm 5VA (TBBA series) Applications: Displays; Chassis; Modems; Power Panels; Power Outlets; Car Batteries; Cash Register Housings; Printer enclosures; remote controls; light boxes; fax machines; projectors; large MFPs; coffee makers; TV front and rear frames and car audio consoles | |||||
General | |||||
Form | Resin Pellets | ||||
Feature | Excellent Processability | ||||
UL Yellow Card E56070-565074 | |||||
Light Covers Printer Parts Panel | |||||
Uses Facsimile machine parts Projector Housing Socket | |||||
Remote Controls Coffee Machine |
|||||
Physical Nominal Value Test Method |
|||||
Density / Specific Gravity 1. 17 g/cm³ ISO 1183 |
|||||
Linear Mold Shrinkage 0.3 - 0.6 % ISO 294 -4 |
|||||
Melt Volume Rate, MVR(220 ºC;10 kg) 48 cm³/ 10 min ISO 1133 |
|||||
Mechanical Nominal Value Test Method |
|||||
Tensile Strength, Break(50 mm/min) 29. 0 MPa ISO 527 -2/50 |
|||||
Tensile Strength, Yield(50 mm/min) 39. 0 MPa ISO 527 -2/50 | |||||
Elongation at Break(50 mm/min) 10 % ISO 527 -2/50 | |||||
Flexural Strength(2 mm/min) 56.0 MPa ISO 178 | |||||
Flexural Modulus(2 mm/min) 1800 MPa ISO 178 | |||||
Izod Impact, Notched ISO 180/1A | |||||
23 °C 22 kJ/m² | |||||
-30 °C 10 kJ/m² | |||||
C harpy Impact, Notched ISO 179 | |||||
23 °C 23 kJ/m² | |||||
-30 °C 10 kJ/m² | |||||
Thermal | Nominal Value | Test Method | |||
Deflection Temperature 1.8 MPa 1.8 MPa |
76.0 °C 84.0 °C |
ISO 75-2/A | |||
Vicat Softening Point 5 kg;50 ºC/hr 50 ºC/hr;1 kg |
79.0 °C 93.0 °C |
ISO 306/B50 ISO 306/A50 |
|||
CTE | 8.48E-5 | ISO 11359 | |||
Flammability, UL94 1.5 mm 2.1 mm 2.1 mm 2.5 mm |
V-1 V-0 5VB 5VA |
UL 94 | |||
Processing | Nominal Value | ||||
Drying Temperature | 80 - 85 °C | ||||
Drying Time | 2.0 - 4.0 hr | ||||
Rear Temperature | 180 - 210 °C | ||||
Middle Temperature | 190 - 220 °C | ||||
Front Temperature | 190 - 220 °C | ||||
Mold Temperature | 40 - 70 °C | ||||
Injection Pressure | 4.90 - 7.85 MPa | ||||
Injection Rate | Slow-Moderate | ||||
Holding Pressure | 1.96 - 4.90 MPa | ||||
Back Pressure | 0.490 - 0.981 MPa | ||||
Cushion | 3.18 mm |