PC Optimum Combination of High Modulus Excellent Impact Strength and Flame Retardance

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC-503R
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

PC Optimum combination of high modulus plus excellent impact strength and flame retardance

Product Description

Product Description
10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV- stabilized. Internal mold release.
General
Form		Resin Pellets
Filler		10 % Glass Fiber
Feature		Outdoor		F1
UL Yellow Card		E121562-220888 E207780-100726439 E45329-100369982
Uses                                          PV Convertor Box              Energy Storage                  smart meter
Physical				Nominal Value	Test Method
Density / Specific Gravity				1.25 g/cm³ 1.245 g/cm³	ASTM D792
Water Absorption(Time 24 hr)				0.12 %	ASTM D570
Moisture Absorption at Equilibrium				0.31 %	ASTM D570
Linear Mold Shrinkage, Flow(Thickness; 3.2 mm)				0.2 - 0.4 %
Hardness, Rockwell M				85	ASTM D785
Hardness, Rockwell R				124	ASTM D785
UV light, water exposure/immersion				f1	UL 746C
Mechanical				Nominal Value	Test Method
Tensile Strength, Break(5 mm/min)				55.0 MPa	ASTM D638-1
Tensile Strength, Yield(5 mm/min)				66.0 MPa	ASTM D638-1
Elongation at Break(5 mm/min)				15 %	ASTM D638-1
Elongation at Yield(5 mm/min)				8.0 %	ASTM D638-1
Flexural Yield Strength(1.3 mm/min;50 mm;span)				103 MPa	ASTM D790
Flexural Modulus(1.3 mm/min;50 mm;span)				3440 MPa	ASTM D790
Izod Impact, Notched(Temperature; 23 °C)				106 J/m	ASTM D256
Izod Impact, Unnotched(Temperature; 23 °C;80x10x3 mm)				2136 J/m	ASTM D4812
Tensile Impact Strength				157 kJ/m²	ASTM D1822S
Dart Drop, Total Energy				101 J	ASTM D3029
Taber Abrasion, mg/1000 Cycles(1 kg;1.0e+3 Cycles;CS- 17 Wheel)				11 mg	ASTM D1044
Thermal				Nominal Value	Test Method
CTE, Flow(Temperature; -40 - 95 °C)				32.4 µm/m-°C	ASTM E831
Specific Heat Capacity				1.21 J/g-°C	ASTM C351
Thermal Conductivity				0.200 W/m-K	ASTM C177
Deflection Temperature Thickness; 6.4 mm;Pressure; 0.46 MPa Thickness; 6.4 mm;Pressure; 1.8 MPa				146 °C 142 °C	ASTM D648
Vicat Softening Point(Rate B/50)				154 °C	ASTM D1525
UL RTI, Electrical				120 °C	UL 746B
UL RTI, Mechanical with Impact				110 °C	UL 746B
UL RTI, Mechanical without Impact				125 °C	UL 746B
Flammability, UL94 Thickness; 1.52 mm Thickness; 2.99 mm				V-0 5VA	UL 94
Oxygen Index				36 %	ASTM D2863
Hot Wire Ignition, HWI				60 - 120 sec	UL 746A
Electrical			Nominal Value			Test Method
Volume Resistivity			> = 1.00e+17 ohms ·cm			ASTM D257
Dielectric Constant Frequency; 1.0e+6 Hz Frequency; 50 - 60 Hz			3.05 3.1			ASTM D150
Dielectric Strength(Thickness; 3.2 mm;In Air)			17.7 kV/mm			ASTM D149
Dissipation Factor Frequency; 50 - 60 Hz Frequency; 1.0e+6 Hz			0.00080 0.0075			ASTM D150
Arc Resistance(Tungsten)			0.00 - 60 sec			ASTM D495
Comparative Tracking Index			100 - 175 V			UL 746A
High Amp Arc Ignition, HAI			60 - 120 arcs			UL 746A
High Voltage Arc-Tracking Rate, HVTR			80.0 - 150 mm/min			UL 746A
Processing						Nominal Value
Injection Molding
Drying Temperature						120 °C
Drying Time						3 - 4 hrs
Drying Time, Cumulative						48 hrs
Maximum Moisture Content						0.02 %
Melt Temperature						310 - 330 °C
Nozzle Temperature						305 - 325 °C
Front - Zone 3 Temperature						310 - 330 °C
Middle - Zone 2 Temperature						300 - 320 °C
Rear - Zone 1 Temperature						290 - 310 °C
Mold Temperature						80 - 115 °C
Back Pressure						0.3 - 0.7 MPa
Screw Speed						40 - 70 rpm
Shot to Cylinder Size						40 - 60 %
Vent Depth						0.025 - 0.076 mm

 
 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 