Polybutylene Terephthalate PBT Resin Particles with High Metal Bonding Strength

• Feature: Plastics
• CAS No.: 63440-93-7
• Formula: C24h24o8
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PBT-WF006NAiQXH
• EINECS: 618-371-8
• Material: Polybutylene Terephthalate/PBT
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Natural Color
• Place of Origin: Guangdong, China
• Use: Radiator Front Cover.Automotive Parts
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Delivery Time: in 7 Days
• Applications: Appliance Handles, Spotlights, Electric Motors.
• Glass Fiber: 30%
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

flame retarded PBT WITH 30% fiberglass reinforced poly butylene terephthalate
   

           

WF006NAiQ-XH is a specialized compound made from iQ PBT, which is known for its excellent properties in NMT (non-magnetic touch) applications. This compound incorporates 30% glass fiber reinforcement to enhance its strength and rigidity. Additionally, it boasts more than 25% post-consumer recycled (PCR) content, making it an environmentally friendly material. Notably, the high metal bonding strength of WF006NAiQ-XH ensures reliable connections in metal assemblies, while its good chemical resistance protects against various chemical substances.

 

General

Form                                        Resin Pellets

Filler                                         30 % Glass Fiber

  25 % Pcr                            Chemical Resistant            Good Dimensional

Feature                                     Excellent Processability     Good Hardness                 Good Metal Adhesion

  Nmt                                   Pcr

Usage                                          Consumer                          Electrical

Physical                                                                                 Nominal Value                                       Test Method

Water Absorption(24 hrs;23 °C)                                          0.04 %                                                    ISO 62-1

Moisture Absorption(23 °C;50% RH/24hrs)                        0.02 %                                                    ISO 62-4

Density / Specific Gravity                                                     1.48 g/cm³                                             ISO 1183

Melt Flow Rate[MFR]                                                                                                                           ASTM D1238

250 °C;5 kgf                                                                         12 g/10min

275°C/5 kgf                                                                        24 g/10min

Melt Volume Rate, MVR                                                                                                                      ISO 1133

5 kg;MVR at 250 °C                                                             9 cm³/10 min

MVR at 275°C/5 kg                                                              19 cm³/10 min

 

 

Mechanical	Nominal Value	Test Method
Izod Impact, Unnotched
23 °C	910 J/m	ASTM D4812
80*10*4;23 °C	51 kJ/m²	ISO 180/1U
Izod Impact, Notched
23 °C	150 J/m	ASTM D256
-30 °C	110 J/m	ASTM D256
80*10*4;23 °C	14.5 kJ/m²	ISO 180/1A
80*10*4;-30 °C	11 kJ/m²	ISO 180/1A
C harpy Impact, Unnotched(23 °C;Edgew;80*10*4;sp =62 mm 0)	56 kJ/m²	ISO 179 1eU
C harpy Impact, V-Notched 23 °C;Edgew;80*10*4;sp =62 mm 0 -30 °C;Edgew;80*10*4;sp =62 mm 0	15 kJ/m² 11 kJ/m²	ISO 179 1eA
Tensile Stress, Break
5 mm/min;Type I	113 MPa	ASTM D638
5 mm/min	111 MPa	ISO 527
Tensile Strain, Break
5 mm/min;Type I	2.7 %	ASTM D638
5 mm/min	2.6 %	ISO 527
Tensile Modulus
5 mm/min	8800 MPa	ASTM D638
1 mm/min	8700 MPa	ISO 527
Flexural Strength
1.3 mm/min;50 mm;span	178 MPa	ASTM D790
2 mm/min	173 MPa	ISO 178
Flexural Modulus
1.3 mm/min;50 mm;span	7770 MPa	ASTM D790
2 mm/min	7400 MPa	ISO 178
Bonding Strength, "T" Treatment, Shear Type	32 MPa	ISO 19095

 

 

Thermal	Nominal Value	Test Method
UL Recognized(≥ 0.7 mm)	HB	UL 94
Vicat Softening Temperature Rate B/50 Rate B/50	150 °C 151 °C	ASTM D1525 ISO 306
Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 0.45 MPa;3.2 mm	172 °C 206 °C	ASTM D648
HDT/Af(1.8)	165 °C	ISO 75/Af
HDT/Bf(0.45)	201 °C	ISO 75/Bf
CTE, Flow -40 - 40 °C -40 - 40 °C	2.4E-05 1/°C 2.4E-05 1/°C	ASTM E831 ISO 11359-2
CTE, XFlow -40 - 40 °C -40 - 40 °C	8.2E-05 1/°C 8.6E-05 1/°C	ASTM E831 ISO 11359-2
Relative Temp Index, Elec	75 °C	UL 746B
Relative Temp Index, Mechanical with Impact	75 °C	UL 746B
Relative Temp Index, Mechanical without Impact	75 °C	UL 746B
Electrical	Nominal Value	Test Method

 

 

Processing	Nominal Value
Drying Temperature<Injection>	100 - 120 °C
Drying Time<Injection>	2 - 4 hrs
Drying Time, Cumulative<Injection>	8 hrs
Maximum Moisture Content<Injection>	0.02 %
Melt Temperature<Injection>	250 - 270 °C
Nozzle Temperature<Injection>	245 - 275 °C
Front, Zone 3 Temperature<Injection>	250 - 270 °C
Middle, Zone 2 Temperature<Injection>	250 - 270 °C
Rear, Zone 1 Temperature<Injection>	240 - 260 °C
Hopper Temperature<Injection>	40 - 60 °C
Mold Temperature<Injection>	100 - 160 °C

Company Profile

Product Parameters

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry