Medical Peek raw Material price per kg PEEK granules GF CF
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html PEEK
Product Description | |||
Application: bar, pipe, profile, optional plating ring, bearing, 3d printing wire. Features: Corrosion resistance, flame retardancy, low smoke resistance, abrasion resistance, wave permeability, excellent electrical insulation properties, high toughness, | |||
General | |||
Form | Resin Pellets | ||
Feature |
Ductile Abrasion Resistant Insulating |
Fda Low Smoke Corrosion Resistant Flame Retardant Transparent To Microwave |
|
Uses | 3d Printing pipe |
Bearings Profiles Chrome plated grill & Trim |
|
Physical | Nominal Value Test Method | ||
Density / Specific Gravity | ISO 1183 | ||
1.3 g/cm³ | |||
1.26 g/cm³ | |||
Durometer Hardness, Shore | D(23 ºC) | 85 ISO 868 | |
Water Absorption at Saturation(23 ºC;3.2 mm 0.07 % | ISO 62-1 | ||
Water Absorption at Equilibrium(23 ºC;3.2 mm | ISO 62-1 | ||
Mold Shrinkage, MD | 1 % | ISO 294-4 | |
Mechanical | Nominal Value | Test Method | |
Tensile Strength, Yield(23 ºC) | 100 MPa | ISO 527 | |
Elongation at Break(23 ºC) | 45 % | ISO 527 | |
Flexural Stress(23 ºC) | 165 MPa | ISO 178 | |
Flexural Modulus(23 ºC) | 4100 MPa | ISO 178 | |
Compressive Strength(23 ºC) | 125 MPa | ||
C harpy Impact Strength, Notched | 7 kJ/m² | ISO 604 | |
Notched Izod Impact Strength | 7.5 kJ/m² | ISO 180 | |
Mold Shrinkage, TD | 1.3 % | ISO 294-4 | |
Thermal | Nominal Value | Test Method | |
Melting Point | 343 °C | ISO 11357 | |
Glass Transition Temp, Tg | 143 °C | ISO 11357 | |
Specific Heat Capacity(23 ºC) | 2.2 kg/ºC | DSC | |
CTE, Flow | 45 ppm/K | ISO 11359 | |
CLTE, Transverse | 120 ppm/K | ISO 11359 | |
Deflection Temperature(1.8 MPa) | 152 °C | ISO 75-f | |
Thermal Conductivity(23 ºC) | 0.29 W/m-K | ISO 22007-4 | |
Melt Flow Rate[MFR](5 kg;380 ºC) | 10 g/10min | ISO 1133 | |
Electrical | Nominal Value | Test Method | |
Dielectric Strength(2mm) | 23 kV/mm | IEC 60243-1 | |
Comparative Tracking Index | 150 V | IEC 60112 | |
Dielectric Constant 23 ºC;1.0e+3 Hz 50 Hz;23 ºC |
3.1 3 |
IEC 60250 | |
Dissipation Factor(23 ºC;1.0e+6 Hz) | 0.004 | IEC 60250 | |
Volume Resistivity 23 ºC;1 V 275 ºC |
1.0E+16 ohms ·cm 1.0E+9 ohms ·cm |
IEC 60093 |