Audited Supplier 923X-XH, an impressive injection molding grade designed with high UV stabilization and excellent impact resistance. Its unique composition comprises non-bromine and non-chlorine flame-retardant systems that offer UL94 V0 @ 1.5mm flame retardancy. Moreover, it exhibits low temperature ductility and impressive processing properties that translate to shorter injection molding cycle times in comparison to standard PC resins. Available in a wide selection of opaque colors, LEXAN923X-XH is a versatile product fit for numerous applications. With its outstanding properties and durability, it is set to revolutionize the world of injection molding.
| General | |||
| Form | Resin Pellets | ||
| Non-Chlorinated Excellent Processability Non-Brominated | |||
| Feature Low Temperature Impact F1 High Impact | |||
| Ductile | |||
| Battery Cases Rail PV Convertor Box Energy Storage |
|||
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity | 1.19 g/cm³ | ASTM D792 | |
| Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) 16 g/10min ASTM D1238 | |||
| Molding Shrinkage, Flow(3.2 mm) 0.40 - 0.80 % Internal Method | |||
| Mechanical | Nominal Value | Test Method | |
| Tensile Modulus(5 mm/min) | 2100 MPa | ASTM D638 | |
| Tensile Strength, Yield(50 mm/min;Type I) 58.0 MPa ASTM D638 | |||
| Tensile Strength, Break(50 mm/min;Type I) 60.0 MPa ASTM D638 | |||
| Tensile Elongation, Yield(50 mm/min;Type I) 6.0 % ASTM D638 | |||
| Tensile Elongation, Break(50 mm/min;Type I) 110 % ASTM D638 | |||
| Flexural Modulus(1.3 mm/min;50 mm;Span) 2400 MPa ASTM D790 | |||
| Flexural Strength, Yield(1.3 mm/min;50 mm;Span) 90.0 MPa ASTM D790 | |||
| Notched Izod Impact | ASTM D256 | ||
| -30 °C | 650 J/m | ||
| 23 °C | 780 J/m | ||
| Instrumented Dart Impact, Total Energy(23 °C) 65.0 J ASTM D3763 | |||
| Thermal | Nominal Value | Test Method |
| Deflection Temperature Under Load, Unannealed(1.8 MPa;3 2 mm) | 123 °C | ASTM D648 |
| Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 140 °C | ASTM D1525 |
| CLTE, Flow(-40 - 40 °C) | 6.1E-5 cm/cm/°C | ASTM E831 |
| CLTE, Transverse(-40 - 40 °C) | 6.2E-5 cm/cm/°C | ASTM E831 |
| RTI Elec | 125 °C | UL 746 |
| RTI Imp | 115 °C | UL 746 |
| RTI Str | 120 °C | UL 746 |
| Flame Rating 1.5 mm 3 mm |
V-0 5VA |
UL 94 |
| Glow Wire Flammability Index(1.5 mm) | 960 °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature [GWIT] 1.5 mm 3 mm |
825 °C 825 °C |
IEC 60695-2-13 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 120 °C | |
| Drying Time<Injection> | 3.0 - 4.0 hr | |
| Suggested Max Moisture<Injection> | 0.020 % | |
| Suggested Shot Size<Injection> | 40 - 60 % | |
| Rear Temperature<Injection> | 270 - 295 °C | |
| Middle Temperature<injection> | 280 - 305 °C | |
| Front Temperature<Injection> | 295 - 315 °C | |
| Nozzle Temperature<Injection> | 290 - 310 °C | |
| Processing Temp, Melt<Injection> | 295 - 315 °C | |
| Mold Temperature<Injection> | 70 - 95 °C | |
| Back Pressure<Injection> | 0.300 - 0.700 MPa | |
| Screw Speed<Injection> | 40 - 70 rpm | |
| Vent Depth<Injection> | 0.025 - 0.076 mm |