High Thermal Conductivity Product Based on Polyamide 6 (PA6) Graphite

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA-GR50
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

High thermal conductivity product based on Polyamide 6 (PA6) Graphite

Product Description

 

Product Description

High thermal conductivity product based on Polyamide 6 (PA6). Graphite.

General

Form                                        Resin Pellets

Filler                                          50 % Graphite

Feature                                     Thermally Conductive

Physical                                                                                 Nominal Value                                       Test Method

Density / Specific Gravity                                                     1.50 g/cm³

Molding Shrinkage, Across Flow(2 mm;60 MPa)                0.40 - 0.60 %

Molding Shrinkage, Flow(2 mm;60 MPa)                           0.35 - 0.65 %

Mechanical                                                                            Nominal Value                                      Test Method

Tensile Modulus(23 °C)                                                        11500 MPa                                            ISO 527-1/2

Tensile Stress, Break(23 °C)                                                 60.0 MPa                                                ISO 527-2/5

Elongation at Break(23 °C)                                                   1.2 %                                                       ISO 527-2/5

C harpy Notched Impact Strength(23 °C)                            3.5 kJ/m²                                                ISO 179 1eA

C harpy Unnotched Impact Strength(23 °C)                        8.0 kJ/m²                                                ISO 179 1eU

Thermal                                                                                 Nominal Value                                      Test Method

Heat Deflection Temperature
 

 

Unannealed;0.45 MPa
Unannealed;1.8 MPa

205 °C
195 °C

 

 

Vicat Softening Temperature	195 °C	ISO 306/B50
CTE, Flow(30 - 100 °C)	1.0E-5 cm/cm/°C
Thermal Conductivity, Through Plane(Longitudinal)	10 W/m-K	Internal Method

Flame Rating
 

 

0.75 mm
1.5 mm

HB
HB

Electrical	Nominal Value	Test Method
Surface Resistivity	1.0E+4 ohms	ASTM D257
Processing		Nominal Value
Melt Temperature		250 - 290 °C
Mold Temperature		80.0 - 100 °C
Drying Temperature		90.0 - 100 °C
Drying Time		3 hr

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....