PA66 BLACK resin is a polyamide 66 alloy designed for injection molding
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | |||||
RS 6600 BLACK resin is a polyamide 66 alloy designed for injection molding. This black grade offers an outstanding dimensional stability, chemical resistance to automotive fluids and is ideal for the realization of complex parts. Main applications: Electric connectors. Sport parts. Automotive fan shrouds. Packaging: This grade is delivered dried in sealed packaging (25kg bags) ready to be processed. Shelf life: Two years from the date of delivery. For one use above this limit, please refer to our technical services. | |||||
General | |||||
Form | Resin Pellets | ||||
Feature | Chemical Resistant Outdoor | Good Dimensional Low Moisture |
Good Thermal | ||
Physical | Nominal Value | Test Method | |||
Density, dry | 1.04 g/cm³ | ISO 1183 | |||
Condition: Density | 1.04 g/cm³ | ISO 1183 | |||
Dry: Melt Volume-Flow Rate, MVR(275 °C;2.16 kg) | 24 cm³/10 min | ASTM D792;ISO 1183;ISO 1133 | |||
Dry: Molding Shrinkage, Across Flow | 1.1 % | ISO 294-4 | |||
Dry: Molding Shrinkage, Flow | 0.50 % | ISO 294-4 | |||
Dry: Water Absorption, Saturation(23 °C) | 2.9 % | ISO 62 | |||
Dry: Water Absorption, Equilibrium(50% RH;23 °C) | 1.2 % | ISO 62 | |||
Dry: Shore Hardness, Shore D(15 sec) | 76 | ISO 7619-1 | |||
Mechanical | Nominal Value | Test Method | |||
Dry: Tensile Modulus | 2330 MPa | ISO 527-2 | |||
Condition: Tensile Modulus | 2200 MPa | ISO 527-2 | |||
Dry: Tensile Stress, Yield | 55.0 MPa | ISO 527-2 | |||
Condition: Tensile Stress, Yield | 52.0 MPa | ISO 527-2 | |||
Dry: Tensile Strain, Yield | 6.0 % | ISO 527-2 | |||
Condition: Tensile Strain, Yield | 10 % | ISO 527-2 | |||
Dry: Nominal Tensile Strain at Break | 15 % | ISO 527-2 | |||
Condition: Nominal Tensile Strain at Break | 20 % | ISO 527-2 | |||
Condition: Tensile creep modulus 1 hr 1.0e+3 hr |
2300 MPa 980 MPa |
ISO 899-1 | |||
Dry: Charpy Notched Impact Strength(23 °C) | 7.0 kJ/m² | ISO 179 1eA | |||
Condition: Charpy Notched Impact Strength(23 °C) | 8.0 kJ/m² | ISO 179 1eA | |||
Condition: Charpy Unnotched Impact Strength(23 °C) | No Break | ISO 179 1eU | |||
Thermal | Nominal Value | Test Method | |||
Dry: Heat Deflection Temperature, Unannealed | |||||
0.45 MPa | 160 °C | ISO 75-2/B | |||
1.8 MPa | 80.0 °C | ISO 75-2/A | |||
Dry: Vicat softening temperature | 170 °C | ISO 306/B50 | |||
Dry: Melting Temperature(10 °C;min) | 255 °C | ISO 11357-3 | |||
Dry: CLTE, Flow | 6.5E-5 cm/cm/°C | ISO 11359-2 | |||
Dry: CLTE, Transverse | 1.1E-4 cm/cm/°C | ISO 11359-2 | |||
Dry: Flammability Classification | IEC 60695-11-10, - 20 | ||||
1.6 mm | HB | ||||
3.2 mm | HB | ||||
Electrical | Nominal Value | Test Method | |||
Condition: Surface resistivity | > 1.0E+15 Ohms | IEC 60093 | |||
Condition: Volume resistivity | > 1.0E+15 Ohms ·cm | IEC 60093 | |||
Dry: Electric Strength | 36 kV/mm | IEC 60243-1 | |||
Condition: Electric Strength | 36 kV/mm | IEC 60243-1 | |||
Condition: Relative Permittivity 100 Hz 1.0e+6 Hz |
3.00 3.00 |
IEC 60250 | |||
Condition: Dissipation factor 100 Hz 1.0e+6 Hz |
0.025 0.017 |
IEC 60250 | |||
Condition: Comparative Tracking Index | 600 V | IEC 60112 | |||
Processing | Nominal Value | ||||
Drying Temperature<Injection> | 80 °C | ||||
Drying Time<Injection> | 4.0 - 8.0 hr | ||||
Processing Temp, Melt<Injection> | 260 - 280 °C | ||||
Mold Temperature<Injection> | 60 - 80 °C |