| Products Information: Medium Temperature Resistance ,10% Glass Fiber, 10% PTFE, 10% Graphite Reinforced Lubrication Specification Products Features: Medium Temperature Resistance,Glass Fiber, PTFE and Graphite Reinforced Lubrication processing methods: Injection |
||
| General | ||
| Form Resin Pellets | ||
| Filler 10 % Glass Fiber | ||
| Feature Internally Lubricated | Good Thermal | |
| Physical | Nominal Value | Test Method |
| Density / Specific Gravity | 1.67 g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 % | ISO 2577;ISO 294- 4 |
| Water Absorption, Equilibrium(50% RH;23 °C) | 0.20 % | ISO 62 |
| Mechanical | Nominal Value | Test Method |
| Tensile Modulus | 4300 MPa | ISO 527-2 |
| Tensile Stress, Break | 85.0 MPa | ISO 527-2 |
| Tensile Strain, Break | 1.2 % | ISO 527-2 |
| Flexural Modulus | 8800 MPa | ISO 178 |
| Flexural Stress | 140 MPa | ISO 178 |
| Notched Izod Impact Strength | 64 kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Test Method |
| Heat Deflection Temperature, Unannealed(1.8 MPa) | 212 °C | ISO 75-2/A |
| Glass Transition Temperature | 217 °C | ISO 11357-2 |
| Flame Rating(1.5 mm) | V-0 | UL 94 |
| Electrical | Nominal Value | Test Method |
| Volume Resistivity | 1.0E+16 ohms ·cm | IEC 60093 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 160 °C | |
| Drying Time<Injection> | 6.0 hr | |
| Processing Temp, Melt<Injection> | 340 - 400 °C | |
| Mold Temperature<Injection> | 135 - 170 °C | |
| Drying Temperature<Extrusion> | 160 °C | |
| Drying Time<Extrusion> | 6.0 hr | |
| Melt Temperature<Extrusion> | 340 - 400 °C | |
| Die Temperature<Extrusion> | 135 - 170 °C | |
Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.
Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.
With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}