LEXAN ML7682 Polycarbonate (PC) is an injection moldable non-chlorinated/brominated, unfilled flame retardant grade with high flow and good heat and impact resistance. It is UV stabilized and has an MVR of 21 (300°C/1.2kg) and a UL94 [email protected], and is available in opaque color options.
Product Description | |||||
LEXAN ML7682 Polycarbonate (PC) is an injection moldable non-chlorinated/brominated, unfilled flame retardant grade with high flow and good heat and impact resistance. It is UV stabilized and has an MVR of 21 (300°C/1.2kg) and a UL94 V[email protected]mm, and is available in opaque color options. | |||||
General | |||||
Form | Resin Pellets | ||||
Low Warpage Good Dimensional Low Moisture Amorphous |
Low Shrinkage Good Thermal Light-Weight Low Creep Sensitivity |
Fda Hydrolysis Resistance Diffusive |
|||
Uses | Packaging | Industria | |||
Physical | Nominal Value | Test Method | |||
Specific Gravity | 1.08 | ASTM D792 | |||
Mold Shrinkage, Flow(3.2 mm) | 0.6 - 0.9 % | SABIC Method | |||
Mechanical | Nominal Value | Test Method | |||
Izod Impact, Notched(23 °C) | 32 J/m | ASTM D256 | |||
Instrumented Dart Impact, Total Energy(23 °C) | 6 J | ASTM D3763 | |||
Tensile Stress, Yield(50 mm/min;Type I) | 86 MPa | ASTM D638 | |||
Tensile Stress, Break(50 mm/min;Type I) | 73 MPa | ASTM D638 | |||
Tensile Strain, Yield(50 mm/min;Type I) | 6 % | ASTM D638 | |||
Tensile Strain, Break(50 mm/min;Type I) | 15 % | ASTM D638 | |||
Tensile Modulus(50 mm/min) | 3000 MPa | ASTM D638 | |||
Flexural Stress, Yield | ASTM D790 | ||||
1.3 mm/min;50 mm;span | 144 MPa | ||||
2.6 mm/min;100 mm;Span | 136 MPa | ||||
Flexural Modulus | ASTM D790 | ||||
1.3 mm/min;50 mm;span | 3150 MPa | ||||
2.6 mm/min;100 mm;Span | 2940 MPa |
Thermal | Nominal Value | Test Method |
Vicat Softening Temperature(Rate B/50) | 173 °C | ASTM D1525 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa 1.82 MPa;6.4 mm |
160 °C 151 °C 151 °C |
ASTM D648 |
CTE, Flow(-40 - 40 °C) | 6.3e-05 1/°C | ASTM E831 |
CTE, XFlow(-40 - 40 °C) | 5.6E-05 1/°C | ASTM E831 |
Processing | Nominal Value | |
Drying Temperature<Sheet Extrusion> | 70 - 80 °C | |
Drying Time<Sheet Extrusion> | 2 - 4 hrs | |
Drying Time, Cumulative<Sheet Extrusion> | 8 hrs | |
Maximum Moisture Content<Sheet Extrusion> | 0 % | |
Melt Temperature<Sheet Extrusion> | 265 - 275 °C | |
Barrel - Zone 1 Temperature<Sheet Extrusion> | 205 - 225 °C | |
Barrel - Zone 2 Temperature<Sheet Extrusion> | 215 - 240 °C | |
Barrel - Zone 3 Temperature<Sheet Extrusion> | 240 - 265 °C | |
Barrel - Zone 4 Temperature<Sheet Extrusion> | 240 - 265 °C | |
Adapter Temperature<Sheet Extrusion> | 240 - 265 °C | |
Die Temperature<Sheet Extrusion> | 240 - 265 °C | |
Roll Stack Temperature, Top<Sheet Extrusion> | 105 - 120 °C | |
Roll Stack Temperature, Middle<Sheet Extrusion> | 105 - 120 °C | |
Roll Stack Temperature, Bottom<Sheet Extrusion> | 105 - 120 °C |