Feature: | Resin Pellets |
---|---|
CAS No.: | 25037-45-0 |
Formula: | 25037-45-0 |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | ||||
Rapidly solidifying standard grade for injection molding. | ||||
General | ||||
Form | ||||
Feature | ||||
UL Yellow Card E41871-233594 |
||||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | ISO 1183 | ||
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 7.5 cm³/10 min | ISO 1133 | ||
Molding Shrinkage, Across Flow | 2.1 % | ISO 294-4 | ||
Molding Shrinkage, Flow | 2.1 % | ISO 294-4 | ||
Water Absorption, Saturation(23 °C) | 0.80 % | ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.20 % | ISO 62 | ||
Ball Indentation Hardness(H 358/30) | 145 MPa | ISO 2039-1 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus | 2700 MPa | ISO 527-2 | ||
Tensile Stress, Yield | 65.0 MPa | ISO 527-2/50 | ||
Tensile Strain, Yield | 9.4 % | ISO 527-2/50 | ||
Nominal Tensile Strain at Break | 27 % | ISO 527-2/50 | ||
Tensile creep modulus(1000 hr;5%;23 °C;strain < = 0) | 1400 MPa | ISO 899-1 | ||
Charpy Notched Impact Strength -30 °C 23 °C |
5.5 kJ/m² 6.0 kJ/m² |
ISO 179 1eA | ||
Charpy Unnotched Impact Strength -30 °C 23 °C |
190 kJ/m² 210 kJ/m² |
ISO 179 1eU | ||
Thermal | Nominal Value | Test Method | ||
Heat Deflection Temperature, Unannealed(1.8 MPa) | 100 °C | ISO 75-2/A | ||
Melting Point | 167 °C | ISO 11357-3 | ||
CLTE, Flow(23 - 55 °C) | 1.1E-4 cm/cm/°C | ISO 11359-2 | ||
Maximum Service Temperature - short cycle operation | 100 °C | |||
Flammability Classification(1.6 mm) | HB | IEC 60695-11-10/- 20 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+13 ohms | IEC 60093 |
Volume Resistivity | 1.0e+15 ohms·cm | IEC 60093 |
Relative Permittivity(1000000 Hz) | 3.80 | IEC 60250 |
Dissipation Factor(1000000 Hz) | 5.0E-3 | IEC 60250 |
Comparative Tracking Index, Solution A | 600 V | IEC 60112 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 100 °C | |
Drying Time<Injection> | 3.0 hr | |
Suggested Max Moisture<Injection> | 0.20 % | |
Hopper Temperature<Injection> | 200 °C | |
Rear Temperature<Injection> | 200 °C | |
Middle Temperature<injection> | 200 °C | |
Front Temperature<Injection> | 200 °C | |
Nozzle Temperature<Injection> | 200 °C | |
Processing Temp, Melt<Injection> | 190 - 230 °C | |
Mold Temperature<Injection> | 60 - 120 °C | |
Residence Time<Injection> | < 10.0 min | |
Screw Speed<Injection> | < 18 m/min |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |