Product Description | ||||
PC0700 resin is a low flow (MFR = 7 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. It is available exclusivPC0700 resin is a low flow (MFR = 7 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. It is available exclusively at |
||||
General | ||||
Form | Resin Pellets | |||
Feature | Outdoor | Low Flow | Good Thermal | |
UL Yellow Card | E207780-101214036 | |||
Uses | Constraction | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792;ISO 1183 | ||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7.0 g/10min | ASTM D1238 | ||
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) | 6.00 cm³/10 min | ISO 1133 | ||
Molding Shrinkage, Flow, Tensile Bar | 0.50 - 0.70 % | Internal Method | ||
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | ||
Water Absorption, Saturation(23 °C) | 0.35 % | ISO 62 | ||
Water Absorption, Equilibrium(23 °C) | 0.35 % | ASTM D570 | ||
Rockwell Hardness, R-Scale | 120 | ASTM D785;ISO 2039-2 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus | ||||
50 mm/min | 2350 MPa 2350 MPa |
ASTM D638 ISO 527-2/1 |
||
Tensile Strength, Yield | ||||
50 mm/min;Type I | 63.0 MPa 63.0 MPa |
ASTM D638 ISO 527-2/50 |
||
Tensile Elongation, Yield | ||||
50 mm/min;Type I | 6.0 % 6.0 % |
ASTM D638 ISO 527-2/50 |
||
Tensile Elongation, Break | ||||
50 mm/min;Type I | > 70 % > 70 % |
ASTM D638 ISO 527-2/50 |
||
Flexural Modulus | ||||
1.3 mm/min;50 mm;Span | 2300 MPa | ASTM D790 | ||
2 mm/min | 2300 MPa | ISO 178 | ||
Flexural Stress, at Yield(2 mm/min) | 90.0 MPa | ISO 178 | ||
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 90.0 MPa | ASTM D790 | ||
Notched Izod Impact | ||||
23 °C | 900 J/m | ASTM D256 | ||
-30 °C;80*10*3 mm | 12 kJ/m² | ISO 180/1A | ||
23 °C;80*10*3 mm | 70 kJ/m² | ISO 180/1A | ||
Unnotched Izod Impact | ||||
23 °C | No Break | ASTM D4812;ISO 180/1U | ||
-30 °C;80*10*3 mm | No Break | ISO 180/1U | ||
Instrumented Dart Impact, Energy at Peak(23 °C) | 65.0 J | ASTM D3763 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Under Load, Unannealed | ||||
0.45 MPa;3.2 mm | 138 °C | ASTM D648 | ||
1.8 MPa;3.2 mm | 127 °C | ASTM D648 | ||
80*10*4 mm;0.45 MPa;4 mm;64 mm;Span | 138 °C | ISO 75-2/Bf | ||
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 127 °C | ISO 75-2/Af | ||
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 144 °C | ISO 306/B50;ASTM D1525 | ||
Ball Pressure Test(123 - 127 °C) | Pass | IEC 60695-10-2 | ||
CLTE, Flow | ||||
-40 - 95 °C | 7.0E-5 cm/cm/°C | ASTM E831 | ||
23 - 80 °C | 7.0E-5 cm/cm/°C | ISO 11359-2 | ||
Thermal Conductivity | 0.20 W/m-K | ASTM C177;ISO 8302 | ||
Flame Rating(1.5 mm) | V-2 | UL 94 | ||
Electrical | Nominal Value | Test Method | ||
Volume Resistivity | > 1.0E+15 Ohms ·cm | ASTM D257;IEC 60093 | ||
Dielectric Strength(1.6 mm) | 27 kV/mm | ASTM D149;IEC 60243-1 | ||
Dielectric Constant | ASTM D150;IEC 60250 | |||
60 Hz | 3.00 | |||
1.0e+6 Hz | 3.00 | |||
Dissipation Factor | ASTM D150;IEC 60250 | |||
60 Hz | 1.0E-3 | |||
1.0e+6 Hz | 0.010 | |||
Optical | Nominal Value | Test Method | ||
Refractive Index | 1.586 | ISO 489;ASTM D542 | ||
Transmittance (2.5e+3 µm) | 88.0 - 90.0 % | ASTM D1003 | ||
Haze(2.5e+3 µm) | < 0.800 % | ASTM D1003 | ||
Processing | Nominal Value | |||
Drying Temperature<Injection> | 120 °C | |||
Drying Time<Injection> | 2.0 - 4.0 hr | |||
Suggested Max Moisture<Injection> | 0.020 % | |||
Hopper Temperature<Injection> | 60 - 80 °C | |||
Rear Temperature<Injection> | 270 - 300 °C | |||
Middle Temperature<injection> | 280 - 310 °C | |||
Front Temperature<Injection> | 290 - 320 °C | |||
Nozzle Temperature<Injection> | 280 - 310 °C | |||
Processing Temp, Melt<Injection> | 290 - 320 °C | |||
Mold Temperature<Injection> | 80 - 120 °C |