Product Description |
LNP THERMOCOMP MX95319 compound is based on Polypropylene (PP) resin containing 20% glass fiber. |
General |
Form Resin Pellets |
Filler 20 % Glass Fiber |
Feature Good Hardness Structural |
Uses Consumer Electrical |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.04 g/cm³ ASTM D792 |
Mold Shrinkage, Flow(24 hrs) 0.4 % ASTM D955 |
Mold Shrinkage, XFlow(24 hrs) 1 % ASTM D955 |
Mechanical Nominal Value Test Method |
Izod Impact, Unnotched(23 °C) 534 J/m ASTM D4812 |
Izod Impact, Notched(23 °C) 42 J/m ASTM D256 |
Tensile Stress, Break 66 MPa ASTM D638 |
Tensile Strain, Break 3.1 % ASTM D638 |
Flexural Stress 103 MPa ASTM D790 |
Flexural Modulus 4130 MPa ASTM D790 |
Thermal Nominal Value Test Method |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) |
145 °C ASTM D648 |
Processing Nominal Value |
Drying Temperature<Injection> 80 °C |
Drying Time<Injection> 4 hrs |
Melt Temperature<Injection> 225 - 250 °C |
Front, Zone 3 Temperature<Injection> 240 - 250 °C |
Middle, Zone 2 Temperature<Injection> 215 - 225 °C |
Rear, Zone 1 Temperature<Injection> 195 - 205 °C |
Mold Temperature<Injection> 30 - 50 °C |
Back Pressure<Injection> 0.2 - 0.3 MPa |
Screw Speed <Injection> 30 - 60 rpm |