High thermal conductivity product based on Polyamide 6 (PA6) Graphite resin
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description |
High thermal conductivity product based on Polyamide 6 (PA6). Graphite. |
General |
Form Resin Pellets |
Filler 50 % Graphite |
Feature Thermally Conductive |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.50 g/cm³ |
Molding Shrinkage, Across Flow(2 mm;60 MPa) 0.40 - 0.60 % |
Molding Shrinkage, Flow(2 mm;60 MPa) 0.35 - 0.65 % |
Mechanical Nominal Value Test Method |
Tensile Modulus(23 °C) 11500 MPa ISO 527-1/2 |
Tensile Stress, Break(23 °C) 60.0 MPa ISO 527-2/5 |
Elongation at Break(23 °C) 1.2 % ISO 527-2/5 |
C harpy Notched Impact Strength(23 °C) 3.5 kJ/m² ISO 179 1eA |
C harpy Unnotched Impact Strength(23 °C) 8.0 kJ/m² ISO 179 1eU |
Thermal Nominal Value Test Method |
Vicat Softening Temperature | 195 °C | ISO 306/B50 |
CTE, Flow(30 - 100 °C) | 1.0E-5 cm/cm/°C | |
Thermal Conductivity, Through Plane(Longitudinal) | 10 W/m-K | Internal Method |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+4 ohms | ASTM D257 |
Processing | Nominal Value | |
Melt Temperature | 250 - 290 °C | |
Mold Temperature | 80.0 - 100 °C | |
Drying Temperature | 90.0 - 100 °C | |
Drying Time | 3 hr |