Product Description |
Polycarbonate (PC), injection molding, medium viscosity, mold release, UV stabilized, f1 listed, nonreinforced, flame retarded, impact modified, improved hydrolysis resistance, good weatherability, Sb, Cl, and Br-free flame retardant, For: Information technology, Electrical/electronic, |
General |
Form |
Resin Pellets |
Feature Low Temperature Impact F1 Excellent Processability |
Uses Telecommunications Energy Storage |
Physical |
Nominal Value |
Test Method |
Density / Specific Gravity(23 °C) |
1.20 g/cm³ |
ISO 1183 |
Melt Viscosity(300 °C;1.0e+3 s-1) |
240 Pa. s |
ISO 11443-A |
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) |
9.50 cm³/10 min |
ISO 1133 |
Mechanical |
Nominal Value |
Test Method |
Tensile Modulus(1 mm/min;23 °C) |
2300 MPa |
ISO 527-1/-2 |
Tensile Stress, Yield(5 mm/min;23 °C) |
56.0 MPa |
ISO 527-1/-2 |
Tensile Stress, Break(5 mm/min;23 °C) |
61.0 MPa |
ISO 527-1/-2 |
Tensile Strain, Yield(5 mm/min;23 °C) |
5.2 % |
ISO 527-1/-2 |
Tensile Strain, Break(5 mm/min;23 °C) |
130 % |
ISO 527-1/-2 |
Flexural Modulus(2 mm/min;23 °C) |
2400 MPa |
ISO 178 |
Flexural Stress(2 mm/min;23 °C) |
92.0 MPa |
ISO 178 |
Notched Izod Impact Strength |
|
ISO 7391 |
23 °C;3 mm |
62 kJ/m² |
|
-20 °C;3 mm |
40 kJ/m² |
|
Thermal |
Nominal Value |
Test Method |
Heat Deflection Temperature, Unannealed(1.8 MPa) |
115 °C |
ISO 75-1/-2 |
Vicat Softening Temperature(120 °C/h;50 N) |
136 °C |
ISO 306 |
Flame Rating |
|
UL 94 |
1.5 mm |
V-0 |
|
2 mm |
5VB |
|
2.4 mm |
5VB |
|
Processing |
Nominal Value |
Drying Temperature - Dry Air Dryer<Injection> |
110 °C |
Drying Time - Dry Air Dryer<Injection> |
4.0 hr |
Mold Temperature<Injection> |
80 °C |
Standard Melt Temperature<Injection> |
300 °C |