PP compound S3615 is a 15% short glass fiber reinforced polypropylene copolymer compound for injection moulding applications. The compound is UV stabilized and the glass fibers are chemically coupled to the PP matrix. This compound combines a matt surface, good sound dampening and excellent scratch resistance with soft-touch haptics and is especially designed for aesthetical automotive interior applications.PPcompound S3615 is a designated automotive grade | ||
General | ||
Form Resin Pellets | ||
Filler 15 % Glass Fiber | ||
Anti-Scratch Feature |
Low Density Environmentally Sound |
Low Gloss Outdoor |
Uses Automotive Interior | ||
Physical Nominal Value Test Method | ||
Density / Specific Gravity 0.990 g/cm³ ISO 1183 | ||
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) 7.0 g/10min ISO 1133 | ||
Molding Shrinkage(24 hr;3.2 mm;65x65x3.2 mm) 0.50 % Internal Method | ||
Filler Content 15 % Internal Method | ||
Mechanical Nominal Value Test Method | ||
Tensile Modulus 2300 MPa ISO 527-2/1A | ||
Tensile Stress, Yield 35.0 MPa ISO 527-2/1A | ||
Tensile Stress, Break 35.0 MPa ISO 527-2/1A | ||
Tensile Strain, Break 5.0 % ISO 527-2/1A | ||
Flexural Modulus(Type 1A) 2100 MPa ISO 178 | ||
Notched Izod Impact Strength ISO 180/1A | ||
-20 °C 13 kJ/m² | ||
0 °C 20 kJ/m² | ||
23 °C 30 kJ/m² | ||
Thermal Nominal Value Test Method | ||
Heat Deflection Temperature, Unannealed(1.8 MPa) 108 °C ISO 75-2/A | ||
CLTE, Flow(-30 - 100 °C) 5.0E-5 cm/cm/°C ISO 11359-2 |