Feature: | Oxidative Degradable |
---|---|
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html
LNP KONDUIT PX11311U compound is based on Nylon 6 resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative, Improved UV Stability and Non-Brominated, Non-Chlorinated Flame Retardant.
Product Description | |||||
LNP KONDUIT PX11311U compound is based on Nylon 6 resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative, Improved UV Stability and Non-Brominated, Non-Chlorinated Flame Retardant. | |||||
General | |||||
Form | Resin Pellets | ||||
Filler | Glass Fiber | Mineral | |||
Feature |
Thermally Conductive | Outdoor Non-Brominated & Non- Chlorinated Flame Retardant |
|||
UL Yellow Card E45329-101761336 | |||||
Uses | Industria | Electrical | Building and Construction | ||
Physical | Nominal Value | Test Method | |||
Mold Shrinkage, Flow(24 hrs) | 0.45 % | ISO 294 | |||
Mold Shrinkage, XFlow(24 hrs) | 0.65 % | ISO 294 | |||
Density | 1.74 g/cm³ | ISO 1183 | |||
Water Absorption(24 hrs;23 °C) | 0.36 % | ISO 62-1 | |||
Mechanical | Nominal Value | Test Method | |||
Izod Impact, Unnotched(80*10*4;23 °C) | 25 kJ/m² | ISO 180/1U | |||
Izod Impact, Notched(80*10*4;23 °C) | 3 kJ/m² | ISO 180/1A | |||
Tensile Stress, Break(5 mm/min) | 105 MPa | ISO 527 | |||
Tensile Strain, Break(5 mm/min) | 1.7 % | ISO 527 | |||
Tensile Modulus(1 mm/min) | 1.2E+04 MPa | ISO 527 | |||
Flexural Stress, Yield(2 mm/min) | 170 MPa | ISO 178 | |||
Flexural Modulus(2 mm/min) | 1.1E+04 MPa | ISO 178 | |||
Thermal | Nominal Value | Test Method | |||
UL Recognized(≥ 1 mm) | V-0 | UL 94 | |||
Glow Wire Ignition Temperature [GWIT] 1 mm 1.5 mm 1.6 mm 3 mm |
800 °C 775 °C 775 °C 800 °C |
IEC 60695-2-13 |
Glow Wire Flammability Index | IEC 60695-2-12 | |
3 mm | 960 °C | |
1.5 mm | 960 °C | |
1 mm | 960 °C | |
Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm) 209 °C ASTM D648 | ||
CTE, Flow -40 - 40 °C -30°C to 80°C 23°C to 80°C |
3.1E-05 1/°C 3.5e-05 1/°C 3.7E-05 1/°C |
ASTM E831 ISO 11359-2 ISO 11359-2 |
CTE, XFlow -40 - 40 °C -30°C to 80°C 23°C to 80°C |
4.8E-05 1/°C 6.0E-05 1/°C 7.3e-05 1/°C |
ASTM E831 ISO 11359-2 ISO 11359-2 |
Thermal conductivity through plane | ISO 22007-2 | |
60*60*3mm plaque | 0.8 W/m-K | |
?80*3mm discs | 1.1 W/m-K | |
Thermal conductivity in plane | ISO 22007-2 | |
60*60*3mm plaque | 1.5 W/m-K | |
?80*3mm discs | 1.3 W/m-K | |
Ball Pressure Test | IEC 60695-10-2 | |
125°C +/- 2°C | PASSES | |
165°C +/- 2°C | PASSES | |
Vicat Softening Temperature(Rate B/120) | 205 °C | ISO 306 |
HDT/Bf(0.45) | 208 °C | ISO 75/Bf |
HDT/Af(1.8) | 185 °C | ISO 75/Af |
Relative Temp Index, Elec | 120 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 110 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+16 ohms | ASTM D257 |
Dielectric Strength, in Oil(1.6 mm) | 15.9 kV/mm | ASTM D149 |
Comparative Tracking Index, CTI | PLC 0 | UL 746A |
Comparative Tracking Index | 600 V | IEC 60112 |
Hot-wire Ignition, HWI(≥ 1 mm) | PLC 0 | UL 746A |
High Amp Arc Ignition, HAI(≥ 1 mm) | PLC 0 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 4 hrs | |
Maximum Moisture Content<Injection> | 0.15 - 0.25 % | |
Melt Temperature<Injection> | 270 - 295 °C | |
Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 275 °C | |
Mold Temperature<Injection> | 85 - 100 °C | |
Back Pressure<Injection> | 0.2 - 0.3 MPa | |
Screw Speed<Injection> | 20 - 60 rpm |