Px11311 Compound Is Based on Nylon6 Resin Containing Mineral and Glass Fiber

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA6-PX11311
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

PX11311 compound is based on Nylon 6 resin containing mineral and glass fiber

 Heat-conducting nylon

Product Description

Product Description
LNP KONDUIT PX11311 compound is based on Nylon 6 resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative and Non-Brominated, Non-Chlorinated Flame  Retardant.
General
Form		Resin Pellets
Filler		Glass Fiber	Mineral
Feature		Thermally Conductive	Non-Brominated & Non- Chlorinated Flame             Retardant					Non-Chlorinated Electrically Isolative
UL Yellow Card                         E207780-101041511
Uses	Consumer                         Industria   Building and Construction				Electrical
Physical			Nominal Value				Test Method
Density / Specific Gravity			1.74 g/cm³				ASTM D792
Mold Shrinkage, Flow(24 hrs)			0.33 %				ASTM D955
Mold Shrinkage, XFlow(24 hrs)			0.48 %				ASTM D955
Water Absorption(24 hrs;23 °C)			0.25 %				Method
Moisture Absorption(50% RH;23 °C)			0.04 %				ISO 62
Melt Volume Rate, MVR(10 kg;MVR at 300 °C)			49 cm³/10 min				ISO 1133
Mechanical			Nominal Value				Test Method
Izod Impact, Unnotched(23 °C)			183 J/m				ASTM D4812
Izod Impact, Notched(23 °C)			43 J/m				ASTM D256
Tensile Stress, Break(5 mm/min;Type I)			52 MPa				ASTM D638
Tensile Strain, Break(5 mm/min;Type I)			2 %				ASTM D638
Tensile Modulus(5 mm/min)			7240 MPa				ASTM D638
Flexural Stress, break(1.3 mm/min;50 mm;span)			76 MPa				ASTM D790
Flexural Modulus(1.3 mm/min;50 mm;span)			9040 MPa				ASTM D790
Impact Strength			5.3 - 18.2 kJ/m²				ISO R179
Thermal				Nominal Value		Test Method
UL Recognized(≥ 1 mm)				V-0		UL 94
Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm				775 °C 850 °C		IEC 60695-2-13
Glow Wire Flammability Index 3 mm 1 mm				960 °C 960 °C		IEC 60695-2-12
Heat Deflection Temperature[HDT], Unannealed(1.82 MPa;6.4 mm)				199 °C		ASTM D648
CTE, Flow -40 - 40 °C 40°C to 120°C				3.1E-05 1/°C 1.9E-05 1/°C		ASTM E831
CTE, XFlow -40 - 40 °C 40°C to 120°C				4.6E-05 1/°C 6.9e-05 1/°C		ASTM E831
Specific Heat				1.42 J/g-°C		ASTM C351
Thermal conductivity through plane 10*10*3mm sample ?80*3mm discs				1.2 W/m-K 0.99 W/m-K		ASTM E1461-07 ISO 22007-2
Thermal conductivity in plane 25*0.4mm disc ?80*3mm discs				2.1 W/m-K 1.38 W/m-K		ASTM E1461-07 ISO 22007-2
Relative Temp Index, Elec				65 °C		UL 746B
Relative Temp Index, Mechanical with Impact				65 °C		UL 746B
Relative Temp Index, Mechanical without Impact				65 °C		UL 746B
Electrical				Nominal Value			Test Method
Surface Resistivity				> 1.E+15 ohms			ASTM D257
Dielectric Strength, in Oil(1 mm)				> 10 kV/mm			ASTM D149
Dielectric Constant, Dk(1.1e+9 Hz)				4.74			ASTM ES 7-83
Dissipation Factor, Df(1.1e+9 Hz)				7.7E-03			ASTM ES 7-83
Comparative Tracking Index				600 V			IEC 60112
Comparative Tracking Index, CTI				PLC 0			UL 746A
Hot-wire Ignition, HWI ≥ 3 mm ≥ 1 mm				PLC 0 PLC 2			UL 746A
High Amp Arc Ignition, HAI( ≥ 1 mm)				PLC 0			UL 746A
Processing							Nominal Value
Drying Temperature<Injection>							80 °C
Drying Time<Injection>							4 hrs
Maximum Moisture Content<Injection>							0.15 - 0.25 %
Melt Temperature<Injection>							270 - 295 °C
Front, Zone 3 Temperature<Injection>							270 - 290 °C
Middle, Zone 2 Temperature<Injection>							270 - 290 °C
Rear, Zone 1 Temperature<Injection>							260 - 275 °C
Mold Temperature<Injection>							85 - 100 °C
Back Pressure<Injection>							0.2 - 0.3 MPa
Screw Speed <Injection>							20 - 60 rpm

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....