Product Description |
LNP THERMOTUF MX00619 compound is based on Polypropylene (PP) resin containing 15% glass fiber. Added features of this grade include: High Impact. |
General |
Form Resin Pellets |
Filler 15 % Glass Fiber |
Feature High Impact |
Uses Consumer Electrical |
Physical Nominal Value Test Method |
Density / Specific Gravity 0.99 g/cm³ ASTM D792 |
Mold Shrinkage, Flow(24 hrs) 0.2 % ASTM D955 |
Mechanical Nominal Value Test Method |
Izod Impact, Unnotched(23 °C) 336 J/m ASTM D4812 |
Izod Impact, Notched(23 °C) 90 J/m ASTM D256 |
Tensile Stress, Break 37 MPa ASTM D638 |
Tensile Strain, Break 2.6 % ASTM D638 |
Tensile Modulus(50 mm/min) 3140 MPa ASTM D638 |
Flexural Stress 55 MPa ASTM D790 |
Flexural Modulus 2810 MPa ASTM D790 |
Thermal Nominal Value Test Method |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) |
137 °C ASTM D648 |
Processing Nominal Value |
Drying Temperature<Injection> 80 °C |
Drying Time<Injection> 4 hrs |
Melt Temperature<Injection> 225 - 250 °C |
Front, Zone 3 Temperature<Injection> 240 - 250 °C |
Middle, Zone 2 Temperature<Injection> 215 - 225 °C |
Rear, Zone 1 Temperature<Injection> 195 - 205 °C |
Mold Temperature<Injection> 30 - 50 °C |
Back Pressure<Injection> 0.2 - 0.3 MPa |
Screw Speed <Injection> 30 - 60 rpm |