Product Description |
50% Glass Reinforced, PA4T |
General |
Form Resin Pellets |
Filler 50 % Glass Fiber |
UL Yellow Card E47960-102085320 |
Physical Nominal Value Test Method |
Density, dry 1.63 g/cm³ ISO 1183 |
Dry: Molding Shrinkage, Across Flow 0.70 % ISO 294-4 |
Dry: Molding Shrinkage, Flow 0.20 % ISO 294-4 |
Dry: Water Absorption, Equilibrium(50% RH;23 °C) 1.8 % ISO 62 |
Mechanical Nominal Value Test Method |
Dry: Tensile Modulus 17000 MPa ISO 527-2 |
Condition: Tensile Modulus 17000 MPa ISO 527-2 |
Dry: Tensile Stress, Break 280 MPa ISO 527-2 |
Condition: Tensile Stress, Break 230 MPa ISO 527-2 |
Dry: Tensile Strain, Break 2.5 % ISO 527-2 |
Condition: Tensile Strain, Break 2.3 % ISO 527-2 |
Dry: Flexural Modulus 16500 MPa ISO 178 |
Dry: Flexural Stress 380 MPa ISO 178 |
Dry: Charpy Notched Impact Strength(23 °C) 15 kJ/m² ISO 179 1eA |
Dry: Charpy Unnotched Impact Strength(23 °C) 90 kJ/m² ISO 179 1eU |
Thermal Nominal Value Test Method |
Dry: Heat Deflection Temperature, Unannealed(1.8 MPa) 245 °C ISO 75-2/A |
Dry: Melting Temperature(10 °C/min) 315 °C ISO 11357-3 |
Dry: CLTE, Flow 1.6E-5 cm/cm/°C ISO 11359-2 |
Dry: CLTE, Transverse 4.8E-5 cm/cm/°C ISO 11359-2 |
Dry: Flammability Classification(1.5 mm) HB |
IEC 60695-11-10, - 20 |