Product Description | |||
Without halogenes flame retarded glass fiber reinforced injection moulding grade; light colorable; outstanding mechanical and electrical properties. | |||
General | |||
Form | Resin Pellets | ||
Filler | 30 % Glass Fiber | ||
Feature | Non-Brominated & Non- Good Mechanicals Chlorinated Flame |
||
Retardant | |||
Physical | Nominal Value | Test Method | |
Melt Volume Rate, MVR(5 kg;275 ºC) 15 cm³/10 min ISO 1133 | |||
Molding shrinkage, parallel | 0.3 % | ISO 2577;ISO 294- 4 |
|
Molding shrinkage, normal | 0.9 % | ISO 2577;ISO 294- 4 |
|
Water Absorption | 5 % | Sim. to ISO 62 | |
Humidity absorption | 1.7 % | Sim. to ISO 62 | |
Density / Specific Gravity | 1.45E-3 g/cm³ | ISO 1183 |
Mechanical | Nominal Value | Test Method |
Dry: Tensile Modulus | 11000 MPa | ISO 527-1;ISO 527-2 |
Condition: Tensile Modulus | 7500 MPa | ISO 527-1;ISO 527-2 |
Dry: Stress at break | 145 MPa | ISO 527-1;ISO 527-2 |
Condition: Stress at break | 95 MPa | ISO 527-1;ISO 527-2 |
Dry: Strain at break | 3 % | ISO 527-1;ISO 527-2 |
Condition: Strain at break | 5 % | ISO 527-1;ISO 527-2 |
Dry: Charpy Impact Strength 23 °C -30 °C |
70 kJ/m² 55 kJ/m² |
ISO 179/1eU |
Condition: Charpy Impact Strength 23 °C -30 °C |
75 kJ/m² 60 kJ/m² |
ISO 179/1eU |
Dry: Charpy Notched Impact Strength 23 °C -30 °C |
8 kJ/m² 7 kJ/m² |
ISO 179/1eA |
Condition: Charpy Notched Impact Strength 23 °C -30 °C |
11 kJ/m² 7 kJ/m² |
ISO 179/1eA |
Thermal | Nominal Value | Test Method |
Melting Temperature(10 °C/min) | 260 ºC | ISO 11357-1/-3 |
Temp. of deflection under load 1.8 MPa 0.45 MPa |
230 ºC 250 ºC |
ISO 75-1/-2 |
Coeff. of linear therm. expansion, parallel | 22E-6 /K | ISO 11359-1/-2 |
Coeff. of linear therm. expansion, normal | 79E-6 /K | ISO 11359-1/-2 |
Burning Behavior 1.5 mm;nominal thickness 0.4 mm;thickness h |
V-0 5VA |
IEC 60695-11-10 |
Oxygen Index | 37 % | ISO 4589-1/-2 |
Electrical | Nominal Value | Test Method |
Relative Permittivity 1.0e+6 Hz 1.0e+6 Hz |
3.9 4.1 |
IEC 62631-2-1 |
Dissipation Factor 1.0e+6 Hz 1.0e+6 Hz |
1.5E-2 2.9E-2 |
IEC 62631-2-1 |
Volume Resistivity | 1e+11 ohms·cm 1e+8 ohms·cm |
IEC 62631-3-1 |
Surface Resistivity | 1E+13 Ohms | IEC 62631-3-2 |
Electric Strength | 38 kV/mm 30 kV/mm |
IEC 60243-1 |
Comparative Tracking Index | 600 | IEC60112 |
Processing | Nominal Value | |
Melt Temperature | 290 ºC | |
Mold Temperature | 80 ºC | |
Injection Velocity | 200 mm/s | |
Drying Time | 4 h | |
Drying Temperature | 80 ºC | |
Hold pressure time | 10 min |