| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 32131-17-2 |
| Formula: | (C12h22n2o2)N |
| Samples: |
BAG
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier Polyamine Nylon 66 33% Glass Reinforced Heat Stabilized Automotive
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||
| 70G60HSL is a 60% glass fiber reinforced, heat stabilized, lubricated polyamide 66 for injection molding. | ||
| General | ||
| Form Resin Pellets | ||
| Filler 60 % Glass Fiber | ||
| Feature Internally Lubricated Good Thermal | ||
| Physical Nominal Value Test Method | ||
| Density / Specific Gravity 1.70 g/cm³ ISO 1183 | ||
| Water Absorption at Equilibrium 1 % ISO 62 | ||
| Water Absorption at Saturation 3.4 % ISO 62 | ||
| Molding Shrinkage(2 mm) 0.6 % ISO 294-4 | ||
| Mold Shrinkage, MD(2 mm) 0.2 % ISO 294-4 | ||
| Mechanical Nominal Value Test Method | ||
| Dry: Stress at break 230 MPa ISO 527 | ||
| Condition: Stress at break 180 MPa ISO 527 | ||
| Dry: Strain at break 1.6 % ISO 527 | ||
| Condition: Strain at break 2.1 % ISO 527 | ||
| Dry: Tensile Modulus 20000 MPa ISO 527 | ||
| Condition: Tensile Modulus 15000 MPa ISO 527 | ||
| Dry: Charpy Notched Impact Strength ISO 179/1eA | ||
| -30 °C 12 kJ/m² | ||
| 23 °C 11 kJ/m² | ||
| Condition: Charpy Notched Impact Strength ISO 179/1eA | ||
| -30 °C 10 kJ/m² | ||
| 23 °C 12 kJ/m² | ||
| Dry: Charpy Impact Unnotched ISO 179/1eU | ||
| -30 °C 60 kJ/m² | ||
| 23 °C 74 kJ/m² | ||
| Condition: Charpy Impact Unnotched ISO 179/1eU | ||
| -30 °C 58 kJ/m² | ||
| 23 °C 880 kJ/m² | ||
| Thermal | Nominal Value | Test Method |
| Deflection Temperature 0.45 MPa 1.8 MPa |
260 °C 255 °C |
ISO 75 |
| Melting Point(10 °C/min) | 263 °C | ISO 11357-1/-3 |
| Vicat Softening Temperature(50 N) | 250 °C | ISO 306 |
| Processing | Nominal Value | |
| Melt Temperature Range | 285 - 305 °C | |
| Melt Temperature Optimum | 295 °C | |
| Mold temperature range | 70 - 120 °C | |
| Mold Temperature Optimum | 100 °C | |
| Drying Time, Dehumidified Dryer | 2 - 4 h | |
| Drying Temperature | 80 °C | |
| Processing Moisture Content | < 0.2 % | |