| Feature: | Plastics |
|---|---|
| CAS No.: | 25766-59-0 |
| Formula: | C6h4c(CH3)2c6h4oco2-]N |
| Samples: |
BAG
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier polycarbonate Flame retardant Phosphate High Flow Resin Pellets
https://forever-plastics.en.made-in-china.com/product-list-1.html
| Product Description | ||||
| LDS (Laser Direct Structuring), Flame retardant (Phosphate), High Flow, Black color only | ||||
| General | ||||
| Form | Resin Pellets | |||
| Filler | Proprietary Filler | |||
| Feature | Lds | Excellent Processability Laser Markable | ||
| UL Yellow Card E340159-101278822 | ||||
| Uses Laser Direct Structuring Cell Phone Cases | ||||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.27 g/cm³ | ISO 1183 | ||
| Melt Mass-Flow Rate, MFR(260 °C;5 kg) | 29 g/10min | ISO 1133 | ||
| Melt Volume-Flow Rate, MVR(260 °C;5 kg) | 28 cm³/10 min | ISO 1133 | ||
| Molding Shrinkage, Across Flow | 0.40 - 0.60 % | Internal Method | ||
| Molding Shrinkage, Flow | 0.40 - 0.60 % | Internal Method | ||
| Water Absorption, Saturation(23 °C) | 0.35 % | ISO 62 | ||
| Water Absorption, Equilibrium(50% RH;23 °C) | 0.15 % | Internal Method | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Modulus | 2500 MPa | ISO 527-2/1 | ||
| Tensile Stress, Yield | 60.0 MPa | ISO 527-2/50 | ||
| Tensile Strain, Yield | 5.0 % | ISO 527-2/50 | ||
| Tensile Strain, Break | > 50 % | ISO 527-2/50 | ||
| Flexural Modulus(2 mm/min) | 2400 MPa | ISO 178 | ||
| Flexural Stress(2 mm/min) | 90.0 MPa | ISO 178 | ||
| C harpy Notched Impact Strength | ISO 179 | |||
| -30 °C | 20 kJ/m² | |||
| 23 °C | 55 kJ/m² | |||
| C harpy Unnotched Impact Strength | ISO 179 | |||
| -30 °C | No Break | |||
| 23 °C | No Break | |||
| Notched Izod Impact Strength | ISO 180/4A | |||
| -20 °C | 20 kJ/m² | |||
| 23 °C | 55 kJ/m² | |||
| Multi-Axial Instrumented Impact Energy(23 °C) | 40.0 J | ISO 6603-2 | ||
| Thermal | Nominal Value | Test Method | ||
| Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
105 °C 103 °C |
ISO 75-2/B ISO 75-2/A |
||
| Vicat Softening Temperature | 111 °C | ISO 306 | ||
| CLTE, Flow | 6.0E-5 cm/cm/°C | ISO 11359-2 | ||
| CLTE, Transverse | 6.0E-5 cm/cm/°C | ISO 11359-2 | ||
| Flame Rating 0.6 mm 1.5 mm |
V-1 V-1 |
UL 94 | ||
| Electrical | Nominal Value | Test Method | ||
| Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 | ||
| Volume Resistivity | > 1.0E+15 Ohms ·cm | IEC 60093 | ||
| Dielectric Constant(1.0e+6 Hz) | 3.00 | IEC 60250 | ||
| Dissipation Factor(1.0e+6 Hz) | 5.0E-3 | IEC 60250 | ||
| Processing | Nominal Value | |||
| Drying Temperature - Hot Air Dryer<Injection> | 90 - 100 °C | |||
| Drying Time - Hot Air Dryer<Injection> | 4.0 - 6.0 hr | |||
| Rear Temperature<Injection> | 270 - 310 °C | |||
| Middle Temperature<injection> | 270 - 310 °C | |||
| Front Temperature<Injection> | 270 - 310 °C | |||
| Nozzle Temperature<Injection> | 270 - 310 °C | |||
| Mold Temperature<Injection> | 70 - 100 °C | |||