PA6 Flame Retardant Mineral Filled Polyamide 6 Injection Molding Resin

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA6-PK0032E
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 5%-60% Glass Fiber/Mineral
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

PA6 Flame Retardant Mineral Filled Polyamide 6 Injection Molding Resin
 Heat-conducting nylon

Product Description

Product Description
Starflam PK0032E is a Halogen Free Red Phosphorous Free Flame Retardant Mineral Filled Polyamide 6 Injection Molding Resin
General
Form                                        Resin Pellets
Filler                                          Mineral
Feature                                                                                    Chlorinated Flame
Retardant
Physical                                                                                 Nominal Value                                       Test Method
Density / Specific Gravity                                                     1.29 g/cm³                                             ISO 1183
Molding Shrinkage, Flow(4 mm)                                         0.80 %                                                    Internal Method
Water Absorption(24 hr;23 °C)                                            1.6 %                                                      ISO 62
Mechanical                                                                            Nominal Value                                      Test Method
Tensile Modulus                                                                  4700 MPa                                              ISO 527-2/1
Tensile Stress, Yield                                                              67.0 MPa                                               ISO 527-2/5
Tensile Stress, Break                                                            67.0 MPa                                                ISO 527-2/5
Tensile Elongation, Yield(5 mm/min)                                  2.9 %                                                      ASTM D638
Tensile Elongation, Break                                                    3.2 %                                                       ISO 527-2/5
Flexural Modulus(2 mm/min)                                              4100 MPa                                              ISO 178
Flexural Stress, at Break(2 mm/min)                                    101 MPa                                                 ISO 178
Flexural Stress, at Yield(2 mm/min)                                     107 MPa                                                 ISO 178
Flexural strain at break(2 mm/min)                                     6.6 %                                                       ISO 178
Notched Izod Impact Strength(23 °C)                                 4.0 kJ/m²                                               ISO 180/1A
Unnotched Izod Impact Strength(23 °C)                             30 kJ/m²                                                 ISO 180/1U
Thermal                                                                                 Nominal Value                                      Test Method
Heat Deflection Temperature, Unannealed
0.45 MPa;64 mm;Span;80x10x4 mm                                 190 °C                                                     ISO 75-2/Bf
1.8 MPa;64 mm;Span;80x10x4 mm                                   73.0 °C                                                    ISO 75-2/Af
Flame Rating(1.6 mm;E2P Measurement)                          V-2                                                          UL 94
Processing	Nominal Value
Drying Temperature<Injection>	80 °C
Drying Time<Injection>	4.0 hr
Suggested Max Moisture<Injection>	0.20 %
Rear Temperature<Injection>	240 - 250 °C
Middle Temperature<injection>	250 - 260 °C
Front Temperature<Injection>	250 - 270 °C
Processing Temp, Melt<Injection>	250 - 270 °C
Mold Temperature<Injection>	50 - 90 °C

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....