based on Polycarbonate (PC) siloxane copolymer resin and is a UV stabilized
https://forever-plastics.en.made-in-china.com/product-list-1.html
Product Description | |||||||
923X is based on Polycarbonate (PC) siloxane copolymer resin and is a UV stabilized high flow opaque injection molding (IM) grade. This non-chlorinated, non-brominated flame retardant grade has UL-94 V0 @ 1.5mm flame rating, extreme low temperature ductility (-40°C) characteristics and excellent processability, providing opportunities for shorter IM cycle times compared to standard PC. LEXAN 923X resin is available in a wide range of opaque colours and targeted for a wide range of applications. |
|||||||
General | |||||||
Form | Resin Pellets | ||||||
Feature |
Non-Brominated High Impact |
Non-Chlorinated Low Temperature Impact |
Non-Brominated & Non- Chlorinated Flame Retardant |
||||
UL Yellow Card | E207780-101158295 | ||||||
Uses |
Transportation Wire Insulation | Aerospace Rail |
Cell Phone Cases Electrical |
||||
Medical Decorative Parts Automotive | |||||||
nergy orage | |||||||
Physical Nominal Value Test Method | |||||||
Density / Specific Gravity 1.19 g/cm³ | ASTM D792;ISO 1183 | ||||||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) 16 g/10min ASTM D1238 | |||||||
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) 15 cm³/10 min ISO 1133 | |||||||
Molding Shrinkage, Flow(3.2 mm) 0.40 - 0.80 % Internal Method | |||||||
Water Absorption, Saturation(23 °C) 0.40 % ISO 62 | |||||||
Water Absorption, Equilibrium(50% RH;23 °C) 0.15 % ISO 62 | |||||||
Mechanical Nominal Value Test Method | |||||||
Tensile Modulus | |||||||
5 mm/min 2100 MPa ASTM D638 | |||||||
2000 MPa ISO 527-1/1 | |||||||
Tensile Strength, Yield | |||||||
50 mm/min;Type I 58.0 MPa ASTM D638 | |||||||
56.0 MPa ISO 527-2/50 | |||||||
Tensile Strength, Break 50 mm/min;Type I |
60.0 MPa 57.0 MPa |
ASTM D638 ISO 527-2/50 |
|||||
Tensile Elongation, Yield 50 mm/min;Type I |
6.0 % 6.0 % |
ASTM D638 ISO 527-2/50 |
|||||
Tensile Elongation, Break 50 mm/min;Type I |
110 % 110 % |
ASTM D638 ISO 527-2/50 |
|||||
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min |
2400 MPa 2100 MPa |
ASTM D790 ISO 178 |
|||||
Flexural Strength 1.3 mm/min;50 mm;Span 2 mm/min |
90.0 MPa 87.0 MPa |
ASTM D790 ISO 178 |
|||||
C harpy Notched Impact Strength -30 °C;80 23 °C;80 |
35 kJ/m² 70 kJ/m² |
ISO 179/1eA | |||||
C harpy Unnotched Impact Strength -30 °C;80 23 °C;80 |
No Break No Break |
ISO 179/1eU | |||||
Notched Izod Impact -30 °C 23 °C -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
650 J/m 780 J/m 30 kJ/m² 65 kJ/m² |
ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A |
|||||
Unnotched Izod Impact Strength -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
No Break No Break |
ISO 180/1U | |||||
Instrumented Dart Impact, Total Energy(23 °C) | 65.0 J | ASTM D3763 | |||||
Thermal | Nominal Value | Test Method | |||||
Deflection Temperature Under Load, Unannealed 1.8 MPa;3.2 mm 80*10*4 mm;1.8 MPa;4 mm;64 mm;Span |
123 °C 118 °C |
ASTM D648 ISO 75-2/Af |
|||||
Vicat Softening Temperature 50 °C/h;50 N;Rate A;Loading 2 |
140 °C 141 °C 139 °C |
ASTM D1525 ISO 306/B120 ISO 306/B50 |
|||||
CLTE, Flow(-40 - 40 °C) | 6.1E-5 cm/cm/°C | ASTM E831;ISO 11359-2 | |||||
CLTE, Transverse(-40 - 40 °C) | 6.2E-5 cm/cm/°C | ASTM E831;ISO 11359-2 | |||||
RTI Elec | 125 °C | UL 746B | |||||
RTI Imp | 115 °C | UL 746B | |||||
RTI Str | 120 °C | UL 746B | |||||
Flame Rating > 1.5 mm > 3 mm |
V-0 5VA |
UL 94 | |||||
Glow Wire Flammability Index 1.5 mm 3 mm |
960 °C 960 °C |
IEC 60695-2-12 | |||||
Glow Wire Ignition Temperature [GWIT] 1.5 mm 3 mm |
825 °C 825 °C |
IEC 60695-2-13 | |||||
Electrical | Nominal Value | Test Method | |||||
Comparative Tracking Index, CTI | PLC 3 | UL 746A | |||||
Comparative Tracking Index | 150 V | IEC 60112 | |||||
High Amp Arc Ignition, HAI > 1.5 mm > 3 mm |
PLC 1 PLC 0 |
UL 746A | |||||
Hot-wire Ignition, HWI > 1.5 mm > 3 mm |
PLC 3 PLC 2 |
UL 746A | |||||
Processing | Nominal Value | ||||||
Drying Temperature<Injection> | 120 °C | ||||||
Drying Time<Injection> | 3.0 - 4.0 hr | ||||||
Suggested Max Moisture<Injection> | 0.020 % | ||||||
Rear Temperature<Injection> | 270 - 295 °C | ||||||
Middle Temperature<injection> | 280 - 305 °C | ||||||
Front Temperature<Injection> | 295 - 315 °C | ||||||
Nozzle Temperature<Injection> | 290 - 310 °C | ||||||
Processing Temp, Melt<Injection> | 295 - 315 °C | ||||||
Mold Temperature<Injection> | 70 - 95 °C | ||||||
Back Pressure<Injection> | 0.300 - 0.700 MPa | ||||||
Screw Speed <Injection> | 40 - 70 rpm | ||||||
Drying Time, Cumulative<Injection> | 48 hr |