Feature: | Oxidative Degradable |
---|---|
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html30% Glass Reinforced, Heat Stabilized, High Flow
Product Description | |||
Miramid® VE25C is a Polyamide 6 (Nylon 6) material filled with 25% glass fiber. It is available in Europe for injection molding. Important attributes of Miramid® VE25C are: Chemical Resistant Crystalline Fast Molding Cycle Good Stiffness Mold Release Agent Typical applications include: Engineering/Industrial Parts Automotive Construction Applications Electrical/Electronic Applications Sporting Goods | |||
General | |||
Form | Resin Pellets | ||
Filler | 25 % Glass Fiber | ||
Feature |
Excellent Processability Crystalline Enhanced Stiffness Grease Resistant Solvent Resistant Good Stability |
Fuel Resistant High Mechanical Strength And Rigidity |
|
Uses | Building Materials Automotive | Engineering Parts Electrical | Sporting Goods Mechanical Parts |
Physical | Nominal Value | Test Method | |
Dry: Density | 1.32 g/cm³ | ISO 1183 | |
Dry: Water Absorption, Saturation | 7.3 % | ISO 62 | |
Dry: Water Absorption, Equilibrium | 1.8 % | ISO 62 | |
Dry: Viscosity Number | 145 cm³/g | ISO 307;ISO 1628;ISO 1157 |
Mechanical | Nominal Value | Test Method |
Dry: Tensile Modulus | 8000 MPa | ISO 527-2 |
Condition: Tensile Modulus | 5000 MPa | ISO 527-2 |
Dry: Tensile Stress, Break | 160 MPa | ISO 527-2 |
Condition: Tensile Stress, Break | 105 MPa | ISO 527-2 |
Dry: Tensile Strain, Break | 3.0 % | ISO 527-2 |
Condition: Tensile Strain, Break | 6.0 % | ISO 527-2 |
Dry: Tensile Creep Modulus(1000 hr) | 3000 MPa | ISO 899-1 |
Dry: Flexural Stress | 220 MPa | ISO 178 |
Condition: Flexural Stress | 130 MPa | ISO 178 |
Dry: Charpy Notched Impact Strength -30 °C 23 °C |
9.00 kJ/m² 10.0 kJ/m² |
ISO 179 1eA |
Condition: Charpy Notched Impact Strength(23 °C) | 20.0 kJ/m² | ISO 179 1eA |
Dry: Charpy Impact Strength -30 °C 23 °C |
50.0 kJ/m² 70.0 kJ/m² |
ISO 179 1eU |
Condition: Charpy Impact Strength(23 °C) | 100 kJ/m² | ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Dry: Deflection Temperature Under Load 0.45 MPa 1.8 MPa |
215 °C 205 °C |
ISO 75-2 |
Dry: Melting Temperature, DSC | 220 °C | ISO 3146 |
Electrical | Nominal Value | Test Method |
Dry: Volume Resistivity | 1E+11 ohms·cm | IEC 60093 |
Condition: Volume resistivity | 1E+8 ohms·cm | IEC 60093 |
Dry: Dielectric Constant(1000000 Hz) | 3.50 | IEC 60250 |
Condition: Dielectric Constant(1000000 Hz) | 6.00 | IEC 60250 |
Dry: Dissipation Factor(1000000 Hz) | 0.020 | IEC 60250 |
Condition: Dissipation factor(1000000 Hz) | 0.25 | IEC 60250 |
Dry: Comparative Tracking Index | 550 | IEC 60112 |
Processing | Nominal Value | |
Processing Temp, Melt<Injection> | 260 - 290 °C | |
Mold Temperature<Injection> | 80 - 120 °C |