Product Description | ||||
PP copolymer 30% chemically coupled glass fibre reinforced, elastomer modified, good impact strength. Automotives, various applications. | ||||
General | ||||
Form | Resin Pellets | |||
Filler | 30 % Glass Fiber | |||
Feature | Ductile | High Impact | Chemically Coupled | |
Uses | Automotive | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity(23 °C) | 1.13 g/cm³ | ASTM D792 | ||
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 10 g/10min | ASTM D1238 | ||
Molding Shrinkage, Flow | 0.40 - 0.60 % | ASTM D955 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus | 6200 MPa | ASTM D638 | ||
Tensile Strength, Break | 65.0 MPa | ASTM D638 | ||
Tensile Elongation, Break | 5.0 % | ASTM D638 | ||
Flexural Modulus | 5500 MPa | ASTM D790 | ||
Flexural strain at break | 100 % | ASTM D790 | ||
Notched Izod Impact | ASTM D256 | |||
0 °C | 130 J/m | |||
23 °C | 170 J/m | |||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 130 °C | ASTM D648 | ||
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 120 °C | ASTM D1525 | ||
Flame Rating | UL 94 | |||
1.6 mm | HB | |||
3.2 mm | HB |