| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 32131-17-2 |
| Formula: | (C12h22n2o2)N |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier Mineral reinforced, halogen- and phosphorus free flame retardant injection moulding grade.
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | |||||
| TECHNYL PROTECT C 52G1 MX25 GY 7035 is a polyamide 6 based on a non-phosphorous and Non-halogenated flame retardant system, reinforced with 25% of mineral filler, heat stabilized, for injection moulding. This phosphorus and halogen free flame retardant grade offers a robust glow wire resistance. |
|||||
| General | |||||
| Form Resin Pellets | |||||
| Filler 25 % Mineral | |||||
Feature |
Non-Brominated & Non- Chlorinated Flame Retardant |
Arc Resistant Rohs |
Good Thermal | ||
| Uses Electrical Electrical applications | |||||
| Physical Nominal Value Test Method | |||||
| Density, dry 1.38 g/cm³ ISO 1183 | |||||
| Dry: Mold Shrinkage, Transverse 0.60 - 0.70 % ISO 294-4 | |||||
| Dry: Mold Shrinkage, Flow 0.35 - 0.45 % ISO 294-4 | |||||
| Dry: Water Absorption(24 hr;23 °C) 1.1 % ISO 62 | |||||
| Mechanical Nominal Value Test Method | |||||
| Dry: Tensile Modulus 7000 MPa ISO 527-1 | |||||
| Condition: Tensile Modulus 2800 MPa ISO 527-1 | |||||
| Dry: Tensile Stress, Break 70 MPa ISO 527-2 | |||||
| Condition: Tensile Stress, Break 35 MPa ISO 527-2 | |||||
| Dry: Strain at break 2.2 % ISO 527-2 | |||||
| Condition: Strain at break 30 % ISO 527-2 | |||||
| Dry: Flexural Modulus 5500 MPa ISO 178 | |||||
| Condition: Flexural Modulus 2200 MPa ISO 178 | |||||
| Dry: Flexural Stress 100 MPa ISO 178 | |||||
| Condition: Flexural Stress 45 MPa ISO 178 | |||||
| Dry: Charpy Notched Impact Strength(-30 °C) 1.5 kJ/m² ISO 179/1eA | |||||
| Dry: Charpy Unnotched Impact Strength(23 °C) 30 kJ/m² ISO 179/1eU | |||||
| Condition: Charpy Unnotched Impact Strength(23 °C) 70 kJ/m² ISO 179/1eU | |||||
| Thermal | Nominal Value | Test Method | |||
| Dry: Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
200 °C 120 °C |
ISO 75-2/B ISO 75-2/A |
|||
| Dry: Melting Temperature(10 °C/min) | 220 °C | ISO 11357-3 | |||
| Dry: Burning rate(1 mm) | < 100 mm/min | FMVSS 302 | |||
| Dry: Flame Rating 0.75 mm 1.5 mm 3 mm |
V-2 V-2 V-2 |
UL 94 | |||
| Dry: Glow Wire Flammability Index 0.75 mm 1.5 mm 3 mm |
960 ºC 960 ºC 960 ºC |
IEC 60695-2-12 | |||
| Dry: Glow Wire Ignition Temperature 0.75 mm 1.5 mm |
700 ºC 725 ºC |
IEC 60695-2-13 | |||
| Dry: Oxygen index | 29 % | ||||
| Electrical | Nominal Value | Test Method | |||
| Dry: Electric Strength | 34 kV/mm | IEC 60243-1 | |||
| Dry: Comparative Tracking Index | 600 V | IEC 60112 | |||
| Processing | Nominal Value | ||||
| Drying Temperature | 80 °C | ||||
| Suggested Max Moisture | 0.10 % | ||||
| Barrell Temperature - Rear | 230 - 235 °C | ||||
| Barrell Temperature - Middle | 235 - 240 °C | ||||
| Barrell Temperature - Front | 235 - 245 °C | ||||
| Mold Temperature | 60 - 90 °C | ||||