Place of Origin: | Guangdong, China |
---|---|
Use: | Radiator Front Cover.Automotive Parts |
Features: | Lubricated, Good Wear Resistance, Low Friction and |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | |||
Jet Black Extrusion Grade Application: tubular products CHARACTERISTICS: Extrusion molding, Super high impact, High rigid | |||
General | |||
Form | Resin Pellets | ||
Feature High Impact | High Mechanical Strength Ec 1907/2006 (Reach) And Rigidity |
||
Uses | Tubing | ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity(23 °C) | 1.05 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate, MFR(220 °C;10 kg) | 5.7 g/10min | ASTM D1238 | |
Molding Shrinkage, Flow(3.2 mm) | 0.40 - 0.70 % | ASTM D955 | |
Rockwell Hardness, R-Scale(23 °C) | 96 | ASTM D785 | |
Mechanical | Nominal Value | Test Method | |
Tensile Strength(23 °C) | 36.0 MPa | ASTM D638 | |
Flexural Modulus(23 °C) | 1960 MPa | ASTM D790 | |
Flexural Strength(23 °C) | 62.0 MPa | ASTM D790 | |
Notched Izod Impact(23 °C;6.35 mm) | 410 J/m | ASTM D256 | |
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Unannealed(1.8 MPa;6.35 mm;bar 0) | 86.0 °C | ASTM D648 | |
Deflection Temperature Under Load, Annealed(1.8 MPa;80 °C;8 hr) | 96.0 °C | ASTM D648 | |
Vicat Softening Temperature(10 N;Loading 1) | 106 °C | ASTM D1525 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |